Tyco Electronics Corporation 300 Constitution Drive Menlo Park, CA 94025 USA Specification This Issue: Date: Replaces: RW-3032 Issue 1 June 9, 2004 RAYCHEM TAT-125 ADHESIVE LINED TUBING Polyolefin, Flexible, Heat-Shrinkable, Dual Wall 1. SCOPE This specification covers the requirements for one type of flexible, electrical insulating, extruded tubing whose diameter will reduce to a predetermined size upon the application of heat in excess of 121C (250F). 1.1 FORM The tubing shall be flame retarded and shall be black with a thermoplastic hot melt adhesive lining, unless otherwise specified. 2. APPLICABLE DOCUMENTS This specification takes precedence over documents referenced herein. Unless otherwise specified, the latest issue of referenced documents applies. The following documents form a part of this specification to the extent specified herein. 2.1 GOVERNMENT-FURNISHED DOCUMENTS Military Documents MIL-T-83133 MIL-PRF-5606 Skydrol 500B Av Gas (100/130) A-A -694 MIL-STD-104 2.2 JP-8 turbine fuel (NATO type F-34) Hydraulic Fluid, Petroleum Base, Aircraft, Missile and Ordnance Aviation Hydraulic Fluid Aviation Gasoline 5% Na Cl solution Limits for Electrical Insulation Color OTHER PUBLICATIONS American Society for Testing and Materials (ASTM)D 2671Standard Methods of Testing Heat-Shrinkable Tubing for Electrical Use (Copies of ASTM publications may be obtained from the American Society for Testing and Materials, 1916 Race Street, Philadelphia, Pennsylvania 19103.) ISO 846 Plastics-Evaluation of the action of microorganisms If this document is printed it becomes uncontrolled. Check for the latest revision. Page 2 SPECIFICATION RW-3032 ISSUE 1 3. REQUIREMENTS 3.1 MATERIALS 3.2 The tubing shall be fabricated from thermally stabilized, modified polyolefin and shall be crosslinked by irradiation. It shall be homogeneous and essentially free from flaws, defects, pinholes, bubbles, seams, cracks, and inclusions. It shall have an interior coating of thermoplastic adhesive. PROPERTIES The tubing shall meet the requirements of Table 3. 4. QUALITY ASSURANCE PROVISIONS 4.1 CLASSIFICATION OF TESTS 4.1.1 Qualification Tests Qualification tests are those performed on tubing submitted for qualification as a satisfactory product and shall consist of all tests listed in this specification. 4.1.2 Acceptance Tests Acceptance tests are those performed on tubing submitted for acceptance under contract. Acceptance tests shall be: dimensions, longitudinal change, tensile strength, ultimate elongation, secant modulus, flammability (jacket only), and heat shock. Statistical process control data may be used to demonstrate conformance for dimensions. 4.2 SAMPLING INSTRUCTIONS 4.2.1 Qualification Test Samples Qualification test samples shall consist of 50 feet (15 m) of black tubing. Qualification of any size within each size range specified below shall qualify all sizes within that size range. Range of Sizes 1/8 through 1/4 3/8 through 1 1-1/2 through 4 4.2.2 Acceptance Test Sample Acceptance test samples shall consist of not less than 16 feet (5 m) of tubing selected at random from each compound batch or the first sleeving production lot of the batch compound. Physical property tests performed at this time qualify subsequent sleeving lots produced from the same compound batch. 4.3 TEST PROCEDURES Unless otherwise specified, perform tests on specimens which have been fully recovered by conditioning for 5 minutes in a 150 5C (302 9F) oven. Condition the test specimens (and measurement gauges, when applicable) for 3 hours at 23 3C (73 5F) and 50 5 percent relative humidity prior to all testing. Use mechanical convection type ovens in which air passes the specimens at a velocity of 100 to 200 feet (30 to 60 m) per minute. If this document is printed it becomes uncontrolled. Check for the latest revision. SPECIFICATION RW-3032 ISSUE 1 4.3.1 Page 3 Dimensions and Longitudinal Change Measure three 6-inch (150 mm) specimens of tubing, as supplied, for length 1/32 inch ( 1 mm), and inside diameter in accordance with ASTM D 2671. Condition the specimens for 5 minutes in a 150 5C (302 9F) oven, cool to 23 3C (73 5F) and then remeasure. Prior to and after conditioning, the dimensions of the tubing shall be in accordance with Table 1 and the longitudinal change shall be in accordance with Table 3. Dimensions of adhesive thickness shall be taken from specimens which have been hung vertically in the oven during recovery. The adhesive thickness shall be the average determined by measuring a cross section taken 1 inch from each end of the suspended specimen. Care should be taken not to overheat the adhesive so that it drips or flows from the tubing. Calculate the longitudinal change as follows: C = Where: 4.3.2 L1 - L 0 x 100 L0 C = Longitudinal Change [Percent] L0 = Length Before Conditioning [Inches (mm)] L1 = Length After Conditioning [Inches (mm)] Tensile Strength and Ultimate Elongation Determine the tensile strength and ultimate elongation of the tubing in accordance with ASTM D 2671 using 1-inch (25-mm) bench marks, a 1-inch (25-mm) initial jaw separation, and jaw separation speed of 20 2 inches (500 50 mm) per minute. 4.4 REJECTION AND RETEST Failure of any sample of tubing to conform to any one of the requirements of this specification shall be cause for rejection of the lot represented. Tubing which has been rejected may be replaced or reworked to correct the defects and resubmitted for acceptance. Before resubmitting, full particulars concerning previous rejection and action taken to correct the defects shall be furnished to the inspector. 5. PREPARATION FOR DELIVERY 5.1 FORM The tubing shall be supplied in lengths of 48 +1, -0 inches (1220 +25, -0 mm) unless otherwise specified. 5.2 PACKAGING Packaging shall be in accordance with good commercial practice. 5.3 MARKING Each container of tubing shall be permanently and legibly marked with the size, quantity, manufacturer's identification, specification number, and lot number. If this document is printed it becomes uncontrolled. Check for the latest revision. Page 4 SPECIFICATION RW-3032 ISSUE 1 TABLE 1 Tubing Dimensions Dimensions - inches (mm) Size Minimum As Supplied I.D. Maximum Recovered I.D. Nominal Recovered Wall With Adhesive Nominal Recovered Adhesive Thickness 1/8 3/16 1/4 3/8 1/2 3/4 1 1-1/2 2 3 4 .125 (3.17) .187 (4.74) .250 (6.35) .375 (9.50) .500 (12.7) .750 (19.05) 1.00 (25.40) 1.50 (38.10) 2.00 (50.80) 3.00 (76.20) 4.00 (101.60) .062 (1.57) .093 (2.36) .125 (3.17) .187 (4.74) .250 (6.35) .375 (9.50) .500 (12.7) .750 (19.05) 1.000 (25.40) 1.500 (38.10) 2.000 (50.80) .027 (0.68) .028 (0.71) .029 (0.74) .029 (0.74) .030 (0.76) .035 (0.89) .042 (1.06) .047 (1.20) .065 (1.65) .065 (1.65) .070 (1.78) .009 (0.23) .010 (0.25) .005 (0.13) .005 (0.13) .006 (0.15) .006 (0.15) .008 (0.20) .011 (0.28) .022 (0.56) .022 (0.56) .020 (0.51) TABLE 2 Mandrel Dimensions for Bend Testing Tubing Size 1/8" to 1/4" inclusive 3/8" to 3/4" inclusive 1" to 4 " Mandrel Diameter mm. in. 5/16 7.9 1/2 12.7 9/16 14.3 If this document is printed it becomes uncontrolled. Check for the latest revision. SPECIFICATION RW-3032 ISSUE 1 Page 5 TABLE 3 Requirements PROPERTY PHYSICAL Dimensions UNIT REQUIREMENT Inches (mm) Longitudinal Change Tensile Strength Percent psi (MPa) In accordance with Table 1 +1, -5 1500 minimum (10.3) Ultimate Elongation Secant Modulus (Expanded) Percent psi (MPa) Cold Impact at -55 2C (-67 4F) Heat Shock 4 hours at 250 3C (482 5F) --- Heat Resistance 168 hours at 175 2C (347 4F) Followed by test for mandrel bend --- 200 minimum 2.5 x 104 maximum (172) No more than 5 of 10 crack No dripping, flowing or cracking of outer wall --- Color Stability 48 hours at 175 2C (347 4F) ELECTRICAL Dielectric Strength --- MIL-STD-104 Volts/mil (volts/mm) Volume Resistivity ohm-cm 500 minimum (19,680) on dual wall specimen 1014 minimum on dual wall specimen --- CHEMICAL Copper Mirror Corrosion 16 hours at 121 -2C (250 4F) Copper Contact Corrosion --16 hours at 121 2C (250 4F) No removal of copper No pitting or blackening of copper If this document is printed it becomes uncontrolled. Check for the latest revision. TEST METHOD Section 4.3.1 ASTM D 2671 ASTM D 2671 Section 4.3.2 ASTM D 2671 ASTM D 882, 2% strain ASTM D 746 Proc. A Table 2 mandrels ASTM D 2671 ASTM D 2671 Table 2 mandrels 360 bend in 10 2 seconds ASTM D 2671 NOTE 1 ASTM D 2671 ASTM D 2671 ASTM D 2671 Procedure A ASTM D 2671 Procedure B Page 6 SPECIFICATION RW-3032 ISSUE 1 TABLE 3 Requirements (continued) PROPERTY CHEMICAL (continued) Flammability (jacket only) UNIT TYPE 1 TYPE 2 TEST METHOD --- --- ASTM D 2671 Procedure B Water Absorption 24 hours at 23C (73F) Fluid Resistance 24 hours at 23C (73F) in: JP-8 Turbine Fuel (MIL-T-83133) Skydrol 500B Hydraulic Fluid (MIL-PRF-5606) Avaiation Gasoline (100/130) 5% NaCl Water Followed by tests for: Dielectric Strength Percent Selfextinguishing within 1 minute, 25% maximum flag burn 0.5 maximum 0.2 maximum ASTM D 2671 --- --- --- ASTM D 2671 Volts/mil (volts/mm) psi (MPa) 400 minimum (15,760) 1000 minimum (6.9) 400 minimum (15, 760) 1000 minimum (6.9) Tensile Strength Fungus Resistance Followed by tests for: Tensile Strength Ultimate Elongation Dielectric Strength ISO 846 Method B psi (Mpa) percent Volts per mil (volts per mm) 1500 minimum (10.3) 200 minimum 500 minimum (19,680) 1500 minimum (10.3) 200 minimum 500 minimum (19,680) Section 4.3.2 ASTM D 2671 ASTM D 2671 *Trademark of the Monsanto Company NOTE 1: Recover the specimens on the metal mandrels for 10 minutes, minimum, at 150 3C (302 5F) or until the tubing is completely shrunk on the mandrels. If this document is printed it becomes uncontrolled. Check for the latest revision.