Multilayer Ceramic Capacitor General Purpose Features: * High capacitance in given case size Applications: For For For For general digital circuit power supply bypass capacitors consumer electronics telecommunication Part Number Explanation MC0402 Size Inch (mm) Size Dielectric Capacitance N 101 K 500 C Dielectric Capacitance Tolerance Rated Voltage Termination T Packaging Style : 0402 (1005) and 0603 (1608) : N = NP0 (C0G), B = X7R AND F = Y5V : Two significant digits followed by no. of zeros and R is in place of decimal point eg.: 0R5 = 0.5 pF 1R0 = 1 pF 104 = 10 x 104 =100 nF : C = 0.25 pF, D = 0.5 pF, F = 1%, J = 5%, K = 10%, M = 20%, Z = -20 / +80% : Two significant digits followed by no. of zeros. And R is in place of decimal point 100 = 10 VDC 160 = 16 VDC 250 = 25 VDC 500 = 50 V DC 101 = 100 VDC : C=Cu/Ni/Sn (for NP0, X7R, Y5V dielectric) L = Ag/Ni/Sn (for partial NP0 items) : T = 7" reeled Tolerance Rated voltage Termination Packaging Style * Partial NPO items are with Ag/Ni/Sn terminations, please ref to below product range of NPO dielectric for detail. External Dimensions Size Inch (mm) L (mm) W (mm) T (mm) / Symbol 0402 (1005) 1 0.05 0.5 0.05 0.5 0.05 1.6 0.1 0.8 0.1 1.6 +0.15 / -0.1 0.8 +0.15 / -0.1 0603 (1608) Remark MB (mm) N # 0.25 +0.05 / -0.1 0.8 0.07 S - 0.4 0.15 0.8 +0.15 / -0.1 X - www.element14.com www.farnell.com www.newark.com Page <1> 11/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose General Electrical Data Dielectric NP0 X7R Y5V 0.5 pF to 0.039 uF 100 pF to 0.82 uF 10 nF to 0.68 uF Capacitance tolerance** Cap 5 pF: C (0.25 pF) 5 pF < Cap < 10 pF: C (0.25 pF), D (0.5 pF) Cap 10 pF: F (*}1%), G (2%), K (10%) K (10%), M (20%) Z (-20 / +80%) Rated voltage (WVDC) 10 V, 16 V, 25 V, 50 V, 100 V 6.3 V, 10 V, 16 V, 25 V, 50 V, 100 V Tan 8* Cap < 30 pF: Q 400 +20C Cap 30 pF: Q 1,000 Note 1 Size 0402, 0603 Capacitance range* 10 G or R x C 500 x F whichever is less Insulation resistance at Ur Operating temperature -55C to +125C Capacitance characteristic -25C to +85C 30 ppm Termination 15% +30 / -80% Ni / Sn (lead-free termination) * Measured at the condition of 30 to 70% related humidity NP0: Apply 1 0.2 Vrms, 1 MHz 10% for Cap 1,000 pF and 1 0.2 Vrms, 1 kHz 10% for Cap > 1,000 pF, 25C at ambient temperature X7R: Apply 1 0.2 Vrms, 1 kHz 10%, at 25C ambient temperature Y5V: Apply 1 0.2 Vrms, 1 kHz 10%, at 20C ambient temperature ** Preconditioning for Class II MLCC: Perform a heat treatment at 150 10C for 1 hour, then leave in ambient condition for 24 2 hours before measurement Note 1: X7R Rated Voltage D.F 50 V 2.5% 25 V 3.5% Exception of D.F. 3% 0603 0.047 F; 0805 0.18 F, 1206 0.47 F 7% 0603 0.33 F 10% 0402 0.1 F; 0603*0.47 F 3.5% 5% 0402 0.033 F; 0603 0.15 F; 0805 0.68 F 5% 10% 0603 0.68 F 10 V 5% 10% 0402 0.33 F; 0603 0.33 F 6.3 V 10% --- --- 16 V www.element14.com www.farnell.com www.newark.com Page <2> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Note 1: Y5V Rated Voltage D.F 50 V 5% 25 V 5% 16 V (C < 1 F) Exception of D.F. 7% 0603 0.1 F; 0805 0.47 F 7% 0402 0.047 F; 0603 0.1 F; 0805 0.33 F 9% 0402 0.68 F; 0603 0.47 F 7% 9% 0402 0.68 F; 0603 0.68 F 16 V (C 1 F) 9% --- --- 10 V 12.5% --- --- 6.3 V 20% --- --- Capacitance Range (NP0 Dielectric) Dielectric NP0 Size Capacitance Rated Voltage (Vdc) 0402 0603 10 16 25 50 100 10 16 25 50 100 0.5 pF (0R5) N^ N^ N^ N^ N^ S S S S S 0.6 pF (0R6) N^ N^ N^ N^ N^ S S S S S 0.7 pF (0R7) N^ N^ N^ N^ N^ S S S S S 0.8 pF (0R8) N^ N^ N^ N^ N^ S S S S S 0.9 pF (0R9) N^ N^ N^ N^ N^ S S S S S 1 pF (1R0) N^ N^ N^ N^ N^ S S S S S 1.2 pF (1R2) N^ N^ N^ N^ N^ S S S S S 1.5 pF (1R5) N^ N^ N^ N^ N^ S S S S S 1.8 pF (1R8) N^ N^ N^ N^ N^ S S S S S 2.2 pF (2R2) N^ N^ N^ N^ N^ S S S S S 2.7 pF (2R7) N^ N^ N^ N^ N^ S S S S S 3.3 pF (3R3) N^ N^ N^ N^ N^ S S S S S 3.9 pF (3R9) N^ N^ N^ N^ N^ S S S S S 4.7 pF (4R7) N^ N^ N^ N^ N^ S S S S S 5.6 pF (5R6) N^ N^ N^ N^ N^ S S S S S 6.8 pF (6R8) N^ N^ N^ N^ N^ S S S S S 8.2 pF (8R2) N^ N^ N^ N^ N^ S S S S S 10 pF (100) N N N N N S S S S S 12 pF (120) N N N N N S S S S S 15 pF (150) N N N N N S S S S S 18 pF (180) N N N N N S S S S S www.element14.com www.farnell.com www.newark.com Page <3> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Capacitance Range (NP0 Dielectric) Dielectric NP0 Size 0402 0603 10 16 25 50 100 10 16 25 50 100 22 pF (220) N N N N N S S S S S 27 pF (270) N N N N N S S S S S 33 pF (330) N N N N N S S S S S 39 pF (390) N N N N N S S S S S 47 pF (470) N N N N N S S S S S 56 pF (560) N N N N N S S S S S 68 pF (680) N N N N N S S S S S 82 pF (820) N N N N N S S S S S 100 pF (101) N N N N N S S S S S 120 pF (121) N N N N N S S S S S 150 pF (151) N N N N N S S S S S 180 pF (181) N N N N N S S S S S 220 pF (221) N N N N N S S S S S 270 pF (271) N N N N S S S S S 330 pF (331) N N N N S S S S S 390 pF (391) N N N N S S S S S 470 pF (471) N N N N S S S S S 560 pF (561) S S S S S 680 pF (681) S S S S S Capacitance Rated Voltage (Vdc) 820 pF (821) S S S S S 1,000 pF (102) S S S S S 1,200 pF (122) X X X X 1,500 pF (152) X X X X 1,800 pF (182) X X X X 2,200 pF (222) X X X X 2,700 pF (272) X X X X 3,300 pF (332) X X X X 3,900 pF (392) 4,700 pF (472) 5,600 pF (562) 6,800 pF (682) 8,200 pF (822) 0.01uF (103) 0.012 uF (123) 1. The letter in cell is expressed the symbol of product thickness 2. The letter in cell with "^" mark is expressed product with Ag / Ni / Sn terminations www.element14.com www.farnell.com www.newark.com Page <4> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Capacitance Range (X7R Dielectric) Dielectric X7R Size Capacitance Rated Voltage (Vdc) 0402 0603 10 16 25 50 10 16 25 50 100 100 pF (101) N N N N S S S S S 120 pF (121) N N N N S S S S S 150 pF (151) N N N N S S S S S 180 pF (181) N N N N S S S S S 220 pF (221) N N N N S S S S S 270 pF (271) N N N N S S S S S 330 pF (331) N N N N S S S S S 390 pF (391) N N N N S S S S S 470 pF (471) N N N N S S S S S 560 pF (561) N N N N S S S S S 680 pF (681) N N N N S S S S S 820 pF (821) N N N N S S S S S 1,000 pF (102) N N N N S S S S S 1,200 pF (122) N N N N S S S S S 1,500 pF (152) N N N N S S S S S 1,800 pF (182) N N N N S S S S S 2,200 pF (222) N N N N S S S S S 2,700 pF (272) N N N N S S S S S 3,300 pF (332) N N N N S S S S S 3,900 pF (392) N N N N S S S S S 4,700 pF (472) N N N N S S S S S 5,600 pF (562) N N N N S S S S S 6,800 pF (682) N N N N S S S S S 8,200 pF (822) N N N N S S S S S 0.01 F (103) N N N N S S S S S 0.012 F (123) N N N S S S S 0.015 F (153) N N N S S S S 0.018 F (183) N N N S S S S 0.022 F (223) N N N S S S S 0.027 F (273) N N S S S S 0.033 F (333) N N S S S X 0.039 F (393) N N S S S X 0.047 F (473) N N S S S X 0.056 F (563) N N S S S X www.element14.com www.farnell.com www.newark.com Page <5> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Capacitance Range (X7R Dielectric) Dielectric X7R Size Capacitance Rated Voltage (Vdc) 0402 10 16 0.068 F (683) N 0.082 F (823) N 0.10 F (104) N 0603 25 50 10 16 25 50 N S S S X N S S S X N X S S S 0.12 F (124) S S X 0.15 F (154) S S X 0.18 F (184) S S X 0.22 F (224) S S X 0.27 F (274) X X X 0.33 F (334) X X X 0.39 F (394) X X X 0.47 F (474) X X X 100 0.56 F (564) 0.68 F (684) 0.82 F (824) 1. The letter in cell is expressed the symbol of product thickness Capacitance Range (Y5V Dielectric) Dielectric Y5V Size Capacitance Rated Voltage (Vdc) 0402 6.3 0603 10 16 25 50 0.010F (103) N N N 0.015F (153) N N 0.022F (223) N 0.033F (333) 6.3 10 16 25 50 N S S S S N N S S S S N N N S S S S N N N N S S S S 0.047F (473) N N N S S S S 0.068F (683) N N N S S S S 0.10F (104) N N N S S S S 0.15F (154) N S S S S S S S S S 0.22F (224) N N S 0.33F (334) N N S S 0.47F (474) N N S S 0.68F (684) N N S X www.element14.com www.farnell.com www.newark.com Page <6> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Packaging Style and Quantity Size Paper tape 7" reel Thickness (mm) / Symbol 0402 (1005) 0603 (1608) 0.5 0.05 N 10 k 0.8 0.07 S 4k 0.8 +0.15 / -0.1 X 4k Reliability Test Conditions and Requirements No. Item Test Condition Requirements 1. Visual and Mechanical --- * No remarkable defect. * Dimensions to conform to individual specification sheet Class I:NPO 2. Capacitance * Shall not exceed the limits given in the detailed specification Cap 1,000 pF 10.2 Vrms, 1 MHz 10% NPO: Cap 30 pF, Q 1,000; Cap < 30 pF, Q 400 +20C X7R Rated D.F Exception of D.F. Voltage 50 V 2.5% 25 V 3.5% 16 V 3 Q/ D.F. (Dissipation Factor) Cap 1,000 pF 1 0.2 Vrms, 1 KHz 10% Class II: X7R, Y5V Cap 10 F, 1 0.2 Vrms, 1 kHz 10% Cap > 10 F, 0.5 0.2 Vrms, 120 Hz 20% 3% 0603 0.047 F; 0805 0.18 F, 1206 0.47 F 7% 0603 0.33 F 10% 0 4 0 2 *0.1 F; 0603*0.47 F 3.5% 5% 0402 0.033 F; 0603 0.15 F; 0805 0.68 F 5% 10% 0603 0.68 F 10 V 5% 10% 0402 0.33 F; 0603 0.33 F 6.3 V 10% --- --- Y57 Rated Voltage 50 V 5% 25 V 5% D.F Exception of D.F. 7% 0 6 0 3 *0.1 F; 0805*0.47 F 7% 0402 0.047 F; 0603 0.1 F; 0805 0.33 F 9% 0 4 0 2 *0.68 F; 0603*0.47 F 16 V (C < 1 F) 7% 9% 0 4 0 2 *0.68 F; 0603 0.68 F 16 V (C 1 F) 9% --- --- 10 V 12.5% --- --- 6.3 V 20% --- --- www.element14.com www.farnell.com www.newark.com Page <7> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Reliability Test Conditions and Requirements No. Item Test Condition Requirements 4. Dielectric Strength * To apply voltage (100 V) 250%. * Duration: 1 to 5 s * Charge and discharge current less than 50 mA * No evidence of damage or flash over during test 5. Insulation Resistance To apply rated voltage for maximum 120 s 10 G or R x C 500 F whichever is smaller With no electrical load 6. Temperature Coefficient T.C. Operating Temperature T.C. Capacitance Change NPO -55C to 125C at 5C NPO Within 30 ppm/C X7R -55C to 125C at 25C X7R Within 15% -25C to 85C at 20C Y5V Within +30% / -80% Y5V Adhesive Strength of Termination * Pressurizing force : 5 N ( 0603) and 10 N (>0603) * Test time: 10 1 s 8. Vibration Resistance * Vibration frequency: 10 to 55 Hz / minimum * Total amplitude: 1.5 mm * Test time: 6 hours (Two hours each in three mutually perpendicular directions) * No remarkable damage * Cap change and Q/D.F.: To meet initial specification 9. Solderability * Solder temperature: 235 5C * Dipping time: 2 0.5 s 95% minimum coverage of all metalized area 7. 10. 11. Bending Test Resistance to Soldering Heat * The middle part of substrate shall be pressurized by means of the pressurizing rod at a rate of about 1 mm per second until the deflection becomes 1 mm and then the pressure shall be maintained for 5 1 s * Measurement to be made after keeping at room temperature for 24 2 hours * Solder temperature: 270 5C * Dipping time: 10 1 s * Preheating: 120 to 150C for 1 minute before immerse the capacitor in a eutectic solder * Before initial measurement (Class II only): Perform 150 +0 / -10C for 1 hour and then set for 48 4 hours at room temperature * Measurement to be made after keeping at room temperature for 48 4 hours * No remarkable damage or removal of the terminations * No remarkable damage. Cap change: NPO: within 5% or 05 pF whichever is larger X7R, X5R: within 12.5% Y5V: within 30% (This capacitance change means the change of capacitance under specified flexure of substrate from the capacitance measured before the test) * No remarkable damage. Cap change: NPO: within 2.5% or 0.25 pF whichever is larger X7R: within 7.5% Y5V: within 20% * Q/D.F., I.R. and dielectric strength: To meet initial requirements * 25% maximum leaching on each edge www.element14.com www.farnell.com www.newark.com Page <8> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Reliability Test Conditions and Requirements No. Item Test Condition Requirements * Conduct the five cycles according to the temperatures and time. 12. Temperature Cycle Step Temperature (C) Time (minimum) 1 Minimum operating temperature +0 / -3 30 3 2 Room temperature 2 to 3 3 Maximum operating temperature +3 / -0 30 3 4 Room temperature 2 to 3 * Before initial measurement (Class II only): Perform 150 +0 / -10C for 1 hour and then set for 48 4 hrs at room temperature * Measurement to be made after keeping at room temperature for 48 4 hours * No remarkable damage. Cap change: NPO: within 2.5% or 0.25 pF whichever is larger X7R, X5R: within 7.5% Y5V: within 20% * Q/D.F., I.R. and dielectric strength: To meet initial requirements * No remarkable damage. Cap change: NPO: within 2.5% or 0.25 pF whichever is larger X7R: 10 V, within 12.5%; 6.3 V, within 25% Y5V: 10 V, within 30%; 6.3 V, within +30 / -40% Q/D.F. value: NPO: More than 30 pF Q 350, 10 pF C 30pF, Q 275+2.5C Less than 10 pF Q 200+10C X7R 13. Humidity (Damp Heat) Steady State * Test temperature: 40 2C * Humidity: 90 to 95% RH * Test time: 500 +24 / -0 hours * Measurement to be made after keeping at room temperature for 48 4 hours Rated Voltage D.F 50 V 3% 25 V 5% 16 V 5% Exception of D.F. 6% 0603 0.047 F; 0805 0.18 F 14% 0603 0.33 F 15% 0 4 0 2 *0.1 F; 0 6 0 3 *0.47 F 10% 0402 0.033 F; 0603 0.15 F 15% 0603 0.68 F 10 V 7.5% 15% 0402 0.33 F; 0603 0.33 F 6.3 V 10% --- --- www.element14.com www.farnell.com www.newark.com Page <9> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Reliability Test Conditions and Requirements No. Item Test Condition Requirements Y5V 13. Humidity (Damp Heat) Steady State * Test temperature: 40 2C * Humidity: 90 to 95% RH * Test time: 500 +24 / -0 hours * Measurement to be made after keeping at room temperature for 48 4 hours Rated Voltage D.F 50 V 7.5% 25 V Exception of D.F. 10% 0 6 0 3 *0.1 F; 0805*0.47 F 10% 0402 0.047 F; 0603 0.1 F; 15% 0 4 0 2 *0.68 F; 0603*0.47 F 7.5% 0 4 0 2 *0.68 F; 0603*0.68 16 V (C < 10% 12.5% 1 F) F 10 V 20% --- --- 6.3 V 30% --- --- I.R.: 10 V, 1 G or R x C 50 -F whichever is smaller 6.3 V, R x C 10 -F * No remarkable damage. Cap change: NPO: 7.5% or 0.75 pF whichever is larger X7R: 10 V, within 12.5%; 6.3 V, within 25% Y5V: 10 V, within 30%; 6.3 V, within +30 / -40% Q/D.F. value: NPO: C 30 pF, Q 200; C <30 pF, Q 100+10 / 3C 14. Humidity (Damp Heat) Load Rated Voltage D.F 50 V 3% 25 V 5% 16 V 5% * Test temperature: 40 2C * Humidity: 90 to 95% RH * Test time: 500 +24 / -0 hours * To apply voltage: rated voltage * Measurement to be made after keeping at room temperature for 48 4 hours Exception of D.F. 6% 0603 0.047 F; 0805 0.18 F; 1206 0.47 F 14% 0603 0.33 F 15% 0 4 0 2 *0.1 F; 0 6 0 3 *0.47 F 10% 0402 0.033 F; 0603 0.15 F; 0805 0.68 F 15% 0603 0.68 F 10 V 7.5% 15% 0402 0.56 F; 0603 0.33 F 6.3 V 10% --- --- www.element14.com www.farnell.com www.newark.com Page <10> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Reliability Test Conditions and Requirements No. Item Test Condition Requirements Y5V 14. Humidity (Damp Heat) Load * Test temperature: 40 2C * Humidity: 90 to 95% RH * Test time: 500 +24 / -0 hours * To apply voltage: rated voltage * Measurement to be made after keeping at room temperature for 48 4 hours Rated Voltage D.F 50 V 7.5% 25 V Exception of D.F. --- --- 10% 0402 0.047 F; 0603 0.1 F; 15% 0 4 0 2 *0.68 F; 0603*0.47 F 7.5% 0 4 0 2 *0.68 F; 0603*0.68 16 V (C < 10% 12.5% 1 F) F 10 V 20% --- --- 6.3 V 30% --- --- I.R.: 10 V, 500 M or R x C 25 -F whichever is smaller 6.3 V, R x C 5 -F * No remarkable damage. Cap change: NPO: 3% or 0.3 pF whichever is larger X7R: 10 V, within 12.5%; 6.3 V, within 25% Y5V: 10 V, within 30%; 6.3 V, within +30 / -40% Q/D.F. value: NPO: More than 30 pF, Q 350 10 pF C < 30 pF, Q 275 +2.5C Less than 10 pF, Q 200 +10C X7R: 15. High Temperature Load (Endurance) * Test temperature: NPO, X7R: 125 3C Y5V: 85 3C * To apply voltage: 200% of rated voltage * Test time: 1,000 +24 / -0 hours * Measurement to be made after keeping at temperature for 48 4 hours Rated Voltage 50 V 25 V 16 V D.F 3% 5% 5% Exception of D.F. 6% 0603 0.047 F 14% 0603 0.33 F 15% 0 4 0 2 *0.1 F; 0 6 0 3 *0.47 F 10% 0402 0.033 F; 0603 0.15 F 15% 0603 0.68 F 10 V 7.5% 15% 0603 0.33 F 6.3 V 10% --- --- www.element14.com www.farnell.com www.newark.com Page <11> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Reliability Test Conditions and Requirements No. Item Test Condition Requirements Y5V: 15. High Temperature Load (Endurance) * Test temperature: NPO, X7R: 125 3C Y5V: 85 3C * To apply voltage: 200% of rated voltage * Test time: 1,000 +24 / -0 hours * Measurement to be made after keeping at temperature for 48 4 hours Rated Voltage D.F 50 V 7.5 % 25 V 7.5 % Exception of D.F. 10% 0603 0.1 F 10% 0402 0.047 F; 0603 0.1 F; 12.5 % 0 4 0 2 *0.68 F; 0 6 0 3 *0.47 F 12.5 % 0 4 0 2 *0.68 F; 0 6 0 3 *0.68 F 16 V (C < 1 F) 10% 10 V 20% --- --- 6.3 V 30% --- --- I.R.: 10 V, 1 G or R x C 50 -F whichever is smaller 6.3 V, R x C 10 -F Tape & Reel Dimensions Fig. 2 The dimensions of paper tape Fig. 3 The dimensions of plastic tape www.element14.com www.farnell.com www.newark.com Page <12> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Size 0402 0603 Thickness N S, X A0 0.62 0.05 1.02 0.05 B0 1.12 0.05 1.8 0.05 T 0.60 0.05 0.95 0.05 K0 - - W 8 0.1 8 0.1 P0 4 0.1 4 0.1 10 x P0 40 0.1 40 0.1 P1 2 0.05 4 0.1 P2 2 0.05 2 0.05 D0 1.55 0.05 1.55 0.05 D1 - - E 1.75 0.05 1.75 0.05 F 3.5 0.05 3.5 0.05 Size 0402 and 0603 Reel size 7" C 13 +0.5 / -0.2 W1 8.4 +1.5 / -0 A 178 0.1 N 60 +1 / -0 Fig. 4 The dimensions of reel Constructions No. Name 1 Ceramic Material 2 Inner Electrode 3 4 NP0* Inner Layer Termination 5 NPO, X7R, Y5V BaTiO3 based AgPd alloy Ni Ag Cu Middle Layer Ni Outer Layer Sn Fig. 5 The construction of MLCC Partial NPO items are with Ag / Ni / Sn terminations, please ref to product range of NPO dielectric for detail www.element14.com www.farnell.com www.newark.com Page <13> 17/02/12 V1.1 Multilayer Ceramic Capacitor General Purpose Storage and Handling Conditions (1) To store products at 5 to 40C ambient temperature and 20 to 70%. related humidity conditions (2) The product is recommended to be used within one year after shipment. Check solderability in case of shelf life extension is needed. Cautions: a. Don.t store products in a corrosive environment such as sulfide, chloride gas, or acid. It may cause oxidization of electrode, which easily be resulted in poor soldering b. To store products on the shelf and avoid exposure to moisture c. Don.t expose products to excessive shock, vibration, direct sunlight and so on Recommended Soldering Conditions The lead-free termination MLCCs are not only to be used on SMT against lead-free solder paste, but also suitable against lead containing solder paste. If the optimized solder joint is requested, increasing soldering time, temperature and concentration of N2 within oven are recommended Fig. 7 Recommended wave soldering profile for SMT process with SnAgCu series solder Fig. 6 Recommended IR reflow soldering profile for SMT process with SnAgCu series solder paste Part Number Table Description Part Number Multilayer Ceramic Capacitor MC0402N101K500CT Important Notice : This data sheet and its contents (the "Information") belong to the members of the Premier Farnell group of companies (the "Group") or are licensed to it. No licence is granted for the use of it other than for information purposes in connection with the products to which it relates. No licence of any intellectual property rights is granted. The Information is subject to change without notice and replaces all data sheets previously supplied. The Information supplied is believed to be accurate but the Group assumes no responsibility for its accuracy or completeness, any error in or omission from it or for any use made of it. Users of this data sheet should check for themselves the Information and the suitability of the products for their purpose and not make any assumptions based on information included or omitted. Liability for loss or damage resulting from any reliance on the Information or use of it (including liability resulting from negligence or where the Group was aware of the possibility of such loss or damage arising) is excluded. This will not operate to limit or restrict the Group's liability for death or personal injury resulting from its negligence. Multicomp is the registered trademark of the Group. (c) Premier Farnell plc 2012. www.element14.com www.farnell.com www.newark.com Page <14> 17/02/12 V1.1