SPECIFICATION
Supplier : Samsung electro-mechanics
Samsung P/N : CL21A106KPCLQNC
Product : Multi-layer Ceramic Capacitor
Description : CAP, 10
, ±10%, 10V, X5R, 0805
CL 21 A 106 K P C L Q N C
Series Samsung Multi-layer Ceramic Capacitor
Size 0805 (inch code) L: 2.0 ± 0.15 mm W: ± 0.15 mm
Thickness division Low profile
Dielectric X5R Inner electrode Ni
Capacitance 10 Termination Cu
Capacitance ±10 % Plating Sn 100% (Pb Free)
tolerance
Product L,W size tolerance change code
Rated Voltage 10 V
Special Reserved for future use
Thickness 0.85 ± 0.1 mm
Packaging Cardboard Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Capacitance Within specified tolerance 1±10% 1.0±0.2Vrms
Tan δ
δδ
δ (DF) 0.1 max.
Insulation 10,000Mohm or 100MohmRated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (×10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X5R
Characterisitcs (From -55 to 85, Capacitance change shoud be within ±15%)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5, 3±0.3sec.
(preheating : 80~120 for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
A. Samsung Part Number
Performance Test condition
250%
1.25
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10 to 55 (return : 1min.)
2hours × 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance
Tan δ :
0.2 max 40±2, 90~95%RH, 500+12/-0hrs
IR : 12.5· or Over
High Temperature Capacitance change : within ±12.5%
With
of the rated voltage
Resistance
Tan δ :
0.2 max Max. operating temperature
IR : 25· or Over
1000+48/-0hrs
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature 25
Max. operating temperature 25
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
Performance Test condition
100%