SCOPE This specification applies to the Pb Free Ceramic Chip Inductors for HFC-1005C-SERIES-SE PRODUCT INDENTIFICATION HFC -1005 C- 30N J Product Code Dimensions Code Ceramic Material Inductance Code Tolerance Code (1) SHAPES AND DIMENSIONS A: 1.000.10 mm B: 0.550.10 mm C: 0.500.10 mm D: 0.20 Typ. mm E: 0.200.10 mm (2) ELECTRICAL SPECIFICATIONS SEE TABLE 1 TEST INSTRUMENTS L,Q : HP 4291B IMPEDANCE ANALYZER (or equivalent) SRF : ENA E5071B NETWORK ANALYZER (or equivalent) RDC : CHROMA MODEL 16502 MILLIOHMMETER (or equivalent) (3) CHARACTERISTICS (3)-1 Ambient temperature ............... 60 Max. (3)-2 Operate temperature range ...... 40105 (Including self temp. rise) (3)-3 Storage temperature range ...... 40105 M AG .LAYER S HFC-1005C-SERIES Page 1/7 TABLE 1 MAGLAYERS Inductance Percent Quality L,Q Freq. SRF DCR IDC PT/NO. L(nH) Tolerance Min. (MHz) (MHz)Min. () Max. (mA) Max. HFC-1005C-1N0 1.0 B,S 13 250 6000 0.045 1360 HFC-1005C-1N8 1.8 B,S 16 250 6000 0.070 1040 HFC-1005C-1N9 1.9 B,S 16 250 6000 0.070 1040 HFC-1005C-2N0 2.0 B,S 16 250 6000 0.070 1040 HFC-1005C-2N2 2.2 B,S 18 250 6000 0.070 960 HFC-1005C-2N4 2.4 B,S 16 250 6000 0.068 790 HFC-1005C-2N7 2.7 B,S 16 250 6000 0.120 640 HFC-1005C-3N3 3.3 B,J,K 20 250 6000 0.066 840 HFC-1005C-3N6 3.6 B,J,K 20 250 6000 0.066 840 HFC-1005C-3N9 3.9 B,J,K 20 250 5800 0.066 840 HFC-1005C-4N3 4.3 B,J,K 18 250 6000 0.091 700 HFC-1005C-4N7 4.7 B,J,K 15 250 4775 0.130 640 HFC-1005C-5N1 5.1 B,J,K 23 250 5800 0.083 800 HFC-1005C-5N6 5.6 B,J,K 23 250 5800 0.083 760 HFC-1005C-6N2 6.2 B,J,K 23 250 5800 0.083 760 HFC-1005C-6N8 6.8 B,J,K 20 250 4800 0.083 680 HFC-1005C-7N5 7.5 B,J,K 25 250 5800 0.104 680 HFC-1005C-8N2 8.2 B,J,K 25 250 4400 0.104 680 HFC-1005C-8N7 8.7 B,J,K 18 250 4100 0.200 480 HFC-1005C-9N0 9.0 B,J,K 25 250 4160 0.104 680 HFC-1005C-9N5 9.5 B,J,K 18 250 4000 0.200 680 HFC-1005C-10N 10 G,J,K 23 250 3900 0.195 480 HFC-1005C-11N 11 G,J,K 26 250 3680 0.120 640 HFC-1005C-12N 12 G,J,K 26 250 3600 0.120 640 HFC-1005C-13N 13 G,J,K 24 250 3450 0.210 560 HFC-1005C-15N 15 G,J,K 26 250 3280 0.172 560 HFC-1005C-16N 16 G,J,K 24 250 3100 0.220 560 HFC-1005C-18N 18 G,J,K 25 250 3100 0.230 420 HFC-1005C-19N 19 G,J,K 26 250 3040 0.202 480 HFC-1005C-20N 20 G,J,K 25 250 3000 0.250 420 HFC-1005C-22N 22 G,J,K 25 250 2800 0.300 400 HFC-1005C-23N 23 G,J,K 26 250 2720 0.214 400 HFC-1005C-24N 24 G,J,K 25 250 2700 0.300 400 HFC-1005C-27N 27 G,J,K 26 250 2480 0.298 400 HFC-1005C-30N 30 G,J,K 25 250 2350 0.300 400 HFC-1005C-33N 33 G,J,K 24 250 2350 0.350 400 HFC-1005C-36N 36 G,J,K 26 250 2320 0.403 320 HFC-1005C-39N 39 G,J,K 25 250 2100 0.550 320 HFC-1005C-40N 40 G,J,K 26 250 2240 0.438 320 HFC-1005C-43N 43 G,J,K 25 250 2030 0.810 230 HFC-1005C-47N 47 G,J,K 26 200 2100 0.830 210 HFC-1005C-51N 51 J,K 25 200 1750 0.820 210 HFC-1005C-56N 56 J,K 22 200 1760 0.970 200 HFC-1005C-68N 68 J,K 22 200 1620 1.120 180 HFC-1005C-82N 82 J,K 20 150 1500 1.250 150 HFC-1005C-R10 100 J,K 20 150 1300 2.520 120 HFC-1005C-R12 120 J,K 20 150 1100 2.660 110 1. Specify the inductance tolerance, B(0.2nH),S(0.3nH),G(2%),J(5%),K(10%) 2.IDC:Based on temperature rise(T:20 Typ.) M AG .LAY E R S HFC-1005C-SERIES Page-2/7 (4) RELIABILITY TEST METHOD Mechanical Characteristics Item Specifications Inductance And Tolerance Measuring Frequency : Within Specified Tolerance Quality Factor Insulation As shown in Product Table Measuring Temperature :+ 25C 1000 mega ohms minimum Resistance Dielectric Test conditions Measured at 100V DC between inductor terminals and center of case. Voltage Measured at 500V AC between inductor No damage occurs when the test terminals and center of case. voltage is applied. for a maximum of 1 minute. Temperature + 25 to 500 ppm /C Over- 40C to + 85C at Coefficient of TCL = L1 - L2 x 106(ppm /C) frequency specified in Product Table. Withstanding Inductance(TCL) L1(T1-T2) Electerical Characteristics Item Specifications Test conditions Component 1005 series - 350g The component shall be reflow soldered Adhesion 1608 series - 1.0Kg onto a P. C. Board ( 240C 5C for (Push Test) Other series - 2012 ~ 3225 20 seconds ). Minimum 1Kg for Pd/Ag Then a dynometer force gauge shall be termination and 2Kg for Mo/Mn applied to any side of the component. termination Drop Test Change In Inductance: The inductor shall be dropped two times on No more than 5% the concrete floor or the vinyl tile from 1M naturally. Thermal Shock Change In Q: Each cycle shall consist of 30 minutes Test No more than 10% at -40C followed by 30 minutes at +85C Change In Appearance: with a 20-second maximum transition time Without distinct damage between temperature extremes. Test duration is 10 cycles. MAG.LAYERS HFC-1005C-SERIES Page-3/7 Endurance Characteristics Item Solderability Specifications Test conditions A minimum of 80% of the metalized Dip pads in flux and dip in solder area must be covered with solder. pot containing lead free solder at 240C 5C for 5 seconds Dip the components into flux and dip Resistance to soldering heat into solder pot containing lead free solder at 260C 5C for 5 2 seconds. Inductors shall be randomly vibrated at amplitude of 1.5mm and frequency of Vibration (Random) 10 - 55 Hz: 0.04 G / Hz for a minimum Change In Inductance: No more than 5% of 15 minutes per axis for each of the three axes. Cold Change In Q: No more than 10% Inductors shall be stored at temperature of Change In Appearance : Without distinct damage Then inductors shall be subjected to Temperature Storage -40C 2C for 1000hrs (+ 48 -0 hrs.) standard atmospheric conditions for 1 hour. After that, measurement shall be made. High Inductors shall be stored at temperature of temperature 85C 2C for 1000hrs (+ 48 -0 hrs.) Storage Then inductors shall be subjected to standard atmospheric conditions for 1 hour. After that, measurement shall be made. Moisture Inductors shall be stored in the chamber Resistance at 45C at 90 - 95 R. H. for 1000 hours. Then inductors are to be tested after 2 hours at room temperature. High Temperature with Loaded Inductors shall be stored in the chamber Inductors must not have a shorted or open winding. at +85C for 1000 hours with rated current applied. Inductors shall be tested at the beginning of test at 500 hours and 1000 hours. Then inductors are to be tested after 1 hour at room temperature. M AG.LAYERS HFC-1005C-SERIES Page-4/7 (5) RECOMMENDED SOLDERING CONDITIONS (Please use this product by reflow soldering) (5)-1 RECOMMENDED FOOTPRINT Unit: mm 1.20 0.45 0.65 (5)-2 RECOMMENED REFLOW PATTERN MAG.LAYERS HFC-1005C-SERIES Page-5/7 (6) PACKAGING (6)-1 CARRIER TAPE DIMENSIONS (mm) P P1 P0 W t W : 8.0 mm P : 2.0 mm P0 : 4.0 mm P1 : 2.0 mm t : 0.7 mm (6)-2 TAPING DIMENSIONS (mm) There shall not continuation more than two vacancies of the product. (6)-3 REEL DIMENSIONS D C B A A : 178 mm B : 60.0 mm C : 13.0 mm D : 12.0 mm E : 9.0 mm E MAG.LAYERS HFC-1005C-SERIES Page-6/7 (6)-4 TOP TAPE PEEL STRENGTH The top tape requires a peel-off force of 0.2 to 0.7N in the direction of the arrow as illustrated below. (6)-5 QUANTITY 10000 pcs/Reel (6)-6 The products are packaged so that no damage will be sustained. (7) ATTENTION IN CASE OF USING In case of using product ,please avoid following matters: Splashing water or salt water Dew condenses Toxic gas (Hydrogen sulfide, Sulfurous acid ,Chlorine, Ammonia) Vibrations or shocks which exceed the specified condition Please be careful for the stress to this product by board flexure or something after the mounting. MAG.LAYERS HFC-1005C-SERIES Page-7/7 TYPICAL ELECTRICAL CHARACTERISTICS MAG.LAYERS HFC-1005C-SERIES ATTACHMENT-1