SCOPE
：
This specification applies to the Pb Free Ceramic Chip Inductors
for HFC-1005C-SERIES-SE
PRODUCT INDENTIFICATION
HFC -1005 C- 30N J
① ② ③ ④ ⑤
① Product Code
② Dimensions Code
③ Ceramic Material
④ Inductance Code
⑤ Tolerance Code
(1) SHAPES AND DIMENSIONS
A: 1.00±0.10 mm
B: 0.55±0.10 mm
C: 0.50±0.10 mm
D: 0.20 Typ. mm
E: 0.20±0.10 mm
(2) ELECTRICAL SPECIFICATIONS
SEE TABLE 1
TEST INSTRUMENTS
L,Q : HP 4291B IMPEDANCE ANALYZER (or equivalent)
SRF : ENA E5071B NETWORK ANALYZER (or equivalent)
RDC : CHROMA MODEL 16502 MILLIOHMMETER (or equivalent)
(3) CHARACTERISTICS
(3)-1 Ambient temperature …............ ＋60℃ Max.
(3)-2 Operate temperature range ...... －40℃～＋105℃
(Including self temp. rise)
(3)-3 Storage temperature range ...... －40℃～＋105℃
HFC-1005C-SERIES Page 1/7
MAG.LAYERS
TABLE 1
Inductance Percent Quality L,Q Freq. SRF DCR IDC
L(nH) Tolerance Min. (MHz) (MHz)Min. (Ω) Max. (mA) Max.
HFC-1005C-1N0□1.0 B,S 13 250 6000 0.045 1360
HFC-1005C-1N8□1.8 B,S 16 250 6000 0.070 1040
HFC-1005C-1N9□1.9 B,S 16 250 6000 0.070 1040
HFC-1005C-2N0□2.0 B,S 16 250 6000 0.070 1040
HFC-1005C-2N2□2.2 B,S 18 250 6000 0.070 960
HFC-1005C-2N4□2.4 B,S 16 250 6000 0.068 790
HFC-1005C-2N7□2.7 B,S 16 250 6000 0.120 640
HFC-1005C-3N3□3.3 B,J,K 20 250 6000 0.066 840
HFC-1005C-3N6□3.6 B,J,K 20 250 6000 0.066 840
HFC-1005C-3N9□3.9 B,J,K 20 250 5800 0.066 840
HFC-1005C-4N3□4.3 B,J,K 18 250 6000 0.091 700
HFC-1005C-4N7□4.7 B,J,K 15 250 4775 0.130 640
HFC-1005C-5N1□5.1 B,J,K 23 250 5800 0.083 800
HFC-1005C-5N6□5.6 B,J,K 23 250 5800 0.083 760
HFC-1005C-6N2□6.2 B,J,K 23 250 5800 0.083 760
HFC-1005C-6N8□6.8 B,J,K 20 250 4800 0.083 680
HFC-1005C-7N5□7.5 B,J,K 25 250 5800 0.104 680
HFC-1005C-8N2□8.2 B,J,K 25 250 4400 0.104 680
HFC-1005C-8N7□8.7 B,J,K 18 250 4100 0.200 480
HFC-1005C-9N0□9.0 B,J,K 25 250 4160 0.104 680
HFC-1005C-9N5□9.5 B,J,K 18 250 4000 0.200 680
HFC-1005C-10N□10 G,J,K 23 250 3900 0.195 480
HFC-1005C-11N□11 G,J,K 26 250 3680 0.120 640
HFC-1005C-12N□12 G,J,K 26 250 3600 0.120 640
HFC-1005C-13N□13 G,J,K 24 250 3450 0.210 560
HFC-1005C-15N□15 G,J,K 26 250 3280 0.172 560
HFC-1005C-16N□16 G,J,K 24 250 3100 0.220 560
HFC-1005C-18N□18 G,J,K 25 250 3100 0.230 420
HFC-1005C-19N□19 G,J,K 26 250 3040 0.202 480
HFC-1005C-20N□20 G,J,K 25 250 3000 0.250 420
HFC-1005C-22N□22 G,J,K 25 250 2800 0.300 400
HFC-1005C-23N□23 G,J,K 26 250 2720 0.214 400
HFC-1005C-24N□24 G,J,K 25 250 2700 0.300 400
HFC-1005C-27N□27 G,J,K 26 250 2480 0.298 400
HFC-1005C-30N□30 G,J,K 25 250 2350 0.300 400
HFC-1005C-33N□33 G,J,K 24 250 2350 0.350 400
HFC-1005C-36N□36 G,J,K 26 250 2320 0.403 320
HFC-1005C-39N□39 G,J,K 25 250 2100 0.550 320
HFC-1005C-40N□40 G,J,K 26 250 2240 0.438 320
HFC-1005C-43N□43 G,J,K 25 250 2030 0.810 230
HFC-1005C-47N□47 G,J,K 26 200 2100 0.830 210
HFC-1005C-51N□51 J,K 25 200 1750 0.820 210
HFC-1005C-56N□56 J,K 22 200 1760 0.970 200
HFC-1005C-68N□68 J,K 22 200 1620 1.120 180
HFC-1005C-82N□82 J,K 20 150 1500 1.250 150
HFC-1005C-R10□100 J,K 20 150 1300 2.520 120
HFC-1005C-R12□120 J,K 20 150 1100 2.660 110
※ 1.□ Specify the inductance tolerance, B(±0.2nH),S(±0.3nH),G(±2%),J(±5%),K(±10%)
2.IDC:Based on temperature rise(△T:20℃ Typ.)
Page-2/7
MAGLAYERS
PT/NO.
HFC-1005C-SERIES
MAG.LAYERS
(4) RELIABILITY TEST METHOD
Mechanical Characteristics
Item Specifications Test conditions
Inductance And Measuring Frequency :
Tolerance As shown in Product Table
Quality Factor Measuring Temperature :+ 25°C
Insulation Measured at 100V DC between inductor
Resistance terminals and center of case.
Dielectric Measured at 500V AC between inductor
Withstanding terminals and center of case.
Voltage for a maximum of 1 minute.
Temperature + 25 to 500 ppm /°C Over- 40°C to + 85°C at
Coefficient of TCL = L1 - L2 x 106(ppm /°C) frequency specified in Product Table.
Inductance(TCL) L1(T1-T2)
Electerical Characteristics
Item Specifications Test conditions
Component 1005 series - 350g The component shall be reflow soldered
Adhesion 1608 series - 1.0Kg onto a P. C. Board ( 240°C ± 5°C for
(Push Test) Other series - 2012 ~ 3225 20 seconds ).
Minimum 1Kg for Pd/Ag Then a dynometer force gauge shall be
termination and 2Kg for Mo/Mn applied to any side of the component.
termination
Drop Test Change In Inductance: The inductor shall be dropped two times on
No more than 5% the concrete floor or the vinyl tile
from 1M naturally.
Thermal Shock Change In Q: Each cycle shall consist of 30 minutes
Test No more than 10% at -40°C followed by 30 minutes at +85°C
Change In Appearance: with a 20-second maximum transition time
Without distinct damage between temperature extremes.
Test duration is 10 cycles.
HFC-1005C-SERIES Page-3/7
Within Specified Tolerance
1000 mega ohms minimum
No damage occurs when the test
voltage is applied.
MAG.LAYERS
Endurance Characteristics
Item Specifications Test conditions
A minimum of 80% of the metalized Dip pads in flux and dip in solder
area must be covered with solder. pot containing lead free solder
at 240°C ± 5°C for 5 seconds
Dip the components into flux and dip
into solder pot containing lead free
solder at 260°C ± 5°C for 5 ± 2 seconds.
Inductors shall be randomly vibrated at
amplitude of 1.5mm and frequency of
10 - 55 Hz: 0.04 G / Hz for a minimum
of 15 minutes per axis for each of
the three axes.
Cold Inductors shall be stored at temperature of
Temperature -40°C ± 2°C for 1000hrs (+ 48 -0 hrs.)
Storage Then inductors shall be subjected to
standard atmospheric conditions for 1 hour.
After that, measurement shall be made.
High Inductors shall be stored at temperature of
temperature 85°C ± 2°C for 1000hrs (+ 48 -0 hrs.)
Storage Then inductors shall be subjected to
standard atmospheric conditions for 1 hour.
After that, measurement shall be made.
Moisture Inductors shall be stored in the chamber
Resistance at 45°C at 90 - 95 R. H. for 1000 hours.
Then inductors are to be tested after
2 hours at room temperature.
High Temperature Inductors shall be stored in the chamber
with Loaded at +85°C for 1000 hours with rated
current applied.
Inductors shall be tested at the beginning
of test at 500 hours and 1000 hours.
Then inductors are to be tested after 1 hour
at room temperature.
Page-4/7
Inductors must not have a shorted or
open winding.
HFC-1005C-SERIES
Solderability
Resistance to
soldering heat
Change In Inductance:
No more than 5%
Change In Q:
No more than 10%
Change In Appearance :
Without distinct damage
Vibration
(Random)
MAG.LAYERS
(5) RECOMMENDED SOLDERING CONDITIONS
(Please use this product by reflow soldering)
(5)-1 RECOMMENDED FOOTPRINT
Unit: mm
(5)-2 RECOMMENED REFLOW PATTERN
HFC-1005C-SERIES Page-5/7
MAG.LAYERS
0.65
0.45
1.20
(6) PACKAGING
(6)-1 CARRIER TAPE DIMENSIONS (mm)
W : 8.0
mm
P : 2.0
mm
P0 : 4.0
mm
P1 : 2.0
mm
t : 0.7 mm
(6)-2 TAPING DIMENSIONS (mm)
There shall not continuation more than two vacancies of the product.
(6)-3 REEL DIMENSIONS
Page-6/7
HFC-1005C-SERIES
A : 178 mm
B : 60.0 mm
C : 13.0 mm
D : 12.0 mm
E : 9.0 mm
MAG.LAYERS
W
PP0P1
t
AB
C
E
D
(6)-4 TOP TAPE PEEL STRENGTH
The top tape requires a peel-off force of 0.2 to 0.7N in
the direction of the arrow as illustrated below.
(6)-5 QUANTITY
10000 pcs/Reel
(6)-6 The products are packaged so that no damage will be sustained.
(7) ATTENTION IN CASE OF USING
In case of using product ,please avoid following matters:
Splashing water or salt water
Dew condenses
Toxic gas (Hydrogen sulfide, Sulfurous acid ,Chlorine, Ammonia)
Vibrations or shocks which exceed the specified condition
Please be careful for the stress to this product by board flexure or something
after the mounting.
Page-7/7
HFC-1005C-SERIES
MAG.LAYERS
TYPICAL ELECTRICAL CHARACTERISTICS
ATTACHMENT-1
HFC-1005C-SERIES
MAG.LAYERS