DISCRETE CERAMICS DATA SHEET www.phycomp-components.com Class 2, X7R 10 V Surface-mount ceramic multilayer capacitors Product specification Supersedes data of 24th May 2000 2001 May 30 Rev.5 Phycomp Product specification Surface-mount ceramic multilayer capacitors FEATURES Class 2, X7R 10 V QUICK REFERENCE DATA * Three standard sizes DESCRIPTION VALUE * For high frequency applications Rated voltage UR (DC) 10 V * Supplied in tape on reel or in bulk case Capacitance range (E6 series) 150 nF to 2.2 F; note 1 Tolerance on capacitance after 1000 hours 10% * NiSn terminations. Test voltage (DC) for 1 minute 2.5 x UR Sectional specifications IEC 60384-10, second edition 1989-04; also based on CECC 32 100 * Tuners Detailed specification based on CECC 32 101-801 * Television receivers End terminations NiSn Climatic category (IEC 60068) 55/125/21 APPLICATIONS Consumer electronics, for example: * Video recorders * All types of cameras. Note 1. Measured at 20 C, 1 V and 1 kHz, using a four-gauge method. DESCRIPTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. terminations ; ;; ; ; ; The inner electrodes are connected to the two terminations and finally covered with a layer of plated tin (NiSn). A cross section of the structure is shown in Fig.1. electrodes MLB457 ceramic material Fig.1 Construction of a ceramic multilayer capacitor. 2001 May 30 Rev.5 2 www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V MECHANICAL DATA W T L4 L2 L3 MBB211 L1 For dimensions see Table 1. Fig.2 Component outline. Physical dimensions Table 1 Capacitor dimensions; see Fig.2 L2 and L3 T CASE SIZE L1 MIN. MAX. MIN. MAX. L4 MIN. W Dimensions in millimetres 0603 1.6 0.10 0.8 0.07 0.73 0.87 0.25 0.65 0.40 0805 2.0 0.10 1.25 0.10 0.50 1.35 0.25 0.75 0.55 1206 3.2 0.15 1.6 0.15 0.50 1.75 0.25 0.75 1.40 Dimensions in inches 0603 0.063 0.004 0.032 0.003 0.029 0.035 0.010 0.026 0.016 1206 0.126 0.006 0.063 0.006 0.020 0.069 0.010 0.030 0.056 0805 0.079 0.004 0.049 0.004 0.020 0.053 0.010 0.030 0.022 2001 May 30 Rev.5 3 www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V SELECTION CHART C (nF) LAST TWO DIGITS OF 12NC 150 52 180 53 220 54 270 55 330 56 390 57 470 58 560 59 680 61 820 62 1000 63 1200 64 1500 65 1800 66 2200 67 10 V 0603 0805 1206 0.80 0.07 0.6 0.10 0.85 0.10 1.25 0.10 Values in shaded cells indicate thickness classification. 0.85 0.10 1.15 0.10 Thickness classification and packing quantities 8 mm TAPE WIDTH QUANTITY PER REEL THICKNESS CLASSIFICATION (mm) 180 mm; 7" QUANTITY PER BULK CASE 330 mm; 13" 0603 PAPER BLISTER PAPER 0805 BLISTER 0.6 0.10 4000 - 20000 - - - 0.80 0.07 4000 - 15000 - 15000 - - 0.85 0.10 4000 - 15000 - - 1.15 0.10 - 3000 - 10000 - - 1.25 0.10 - 3000 - 10000 - 5000 2001 May 30 Rev.5 4 www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V ORDERING INFORMATION Components may be ordered by using either a simple 15-digit clear text code or Phycomp's unique 12NC. Clear text code Example: 06032R154K6BB0D SIZE CODE 0603 TEMP. CHAR. 2R = X7R 0805 1206 CAPACITANCE TOL. 154 = 150000 pF; the third digit signifies the multiplying factor: 4 = x 10000 5 = x 100000 K = 10% VOLTAGE TERMINATION 6 = 10 V B = NiSn PACKING 2 = 180 mm; 7" paper MARKING SERIES 0 = no marking D = BME 3 = 330 mm; 13" paper B = 180 mm; 7" blister F = 330 mm; 13" blister P = bulk case Ordering code 12NC handbook, full pagewidth 2 2 X X X X X X 5 X X X Capacitance value(1) Carrier type 22 blister 38 paper tape 54 bulk Tolerance 6 10% Rated voltage - Termination 24 10 V; NiSn Size 6 0603 0 0805 1 1206 CCB409 Packaging(2) 1 reel: 180 mm; 7" 5 reel: 330 mm; 13" 4 bulk case (1) Refer to chapter "Selection chart". (2) Quantity on reel depends on thickness classification, see section "Thickness classification and packing quantities". 2001 May 30 Rev.5 5 www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V ELECTRICAL CHARACTERISTICS Class 2 capacitors; X7R dielectric; NiSn terminations Unless otherwise stated all electrical values apply at an ambient temperature of 20 1 C, an atmospheric pressure of 86 to 105 kPa, and a relative humidity of 63 to 67%. DESCRIPTION VALUE Capacitance range (E6 series); note 1 150 nF to 2.2 F Tolerance on capacitance after 1000 hours 10% Tan ; note 1 5% Insulation resistance after 1 minute at UR (DC) Rins x C 500 seconds Maximum capacitance change as a function of temperature 15% Ageing typical 3% per time decade Resistance to soldering heat 260 C; 10 seconds Note 1. Measured at 20 C, 1 V and 1 kHz, using a four-gauge method. 2001 May 30 Rev.5 6 www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V TESTS AND REQUIREMENTS Table 2 Test procedures and requirements IEC IEC 60384-10/ 60068-2 CECC 32 100 TEST CLAUSE METHOD TEST PROCEDURE REQUIREMENTS no visible damage the capacitors may be mounted on printed-circuit boards or ceramic substrates by applying wave soldering, reflow soldering (including vapour phase soldering) or conductive adhesive 4.4 mounting 4.5 visual inspection and any applicable method using dimension check x10 magnification in accordance with specification 4.6.1 capacitance f = 1 kHz; measuring voltage 1 Vrms at 20 C within specified tolerance 4.6.2 tan f = 1 kHz; measuring voltage 1 Vrms at 20 C in accordance with specification 4.6.3 insulation resistance at UR (DC) for 1 minute in accordance with specification 4.6.4 voltage proof 2.5 x UR for 1 minute no breakdown or flashover 4.7.1 temperature characteristic between minimum and maximum temperature in accordance with specification 4.8 adhesion a force of 5 N applied for 10 s to the line joining the terminations and in a plane parallel to the substrate no visible damage 4.9 bond strength of plating on end face mounted in accordance with CECC 32 100, paragraph 4.4 no visible damage conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm C/C: 10% precondition: 120 to 150 C for 1 minute; 260 5 C for 10 0.5 s the terminations shall be well tinned after recovery resistance to leaching 260 5 C for 30 1 s in a static solder bath using visual enlargement of x10, dissolution of the terminations shall not exceed 10% solderability zero hour test, and test after storage (20 to 24 months) in original packing in normal atmosphere; unmounted chips completely immersed for 2 0.5 s in a solder bath at 235 5 C the terminations shall be well tinned 4.10 4.11 Tb Ta 2001 May 30 Rev.5 resistance to soldering heat 7 C/C: 10% www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors IEC IEC 60384-10/ 60068-2 CECC 32 100 TEST CLAUSE METHOD 4.12 4.14 Na Ca 4.15 2001 May 30 Rev.5 Class 2, X7R 10 V TEST rapid change of temperature damp heat, steady state endurance PROCEDURE REQUIREMENTS preconditioning; 5 cycles in the following sequence: 30 minutes at -55 C, change within 30 minutes to +125 C no visible damage after 48 hours recovery: initialization: 48 hours after UR at 40 C for 1 hour (for initial value measurement); 500 12 hours at 40 C; 90 to 95% RH; UR applied preconditioning: UR at 40 C for 1 hour initialization: 2 x UR at 125 C for 1 hour (initial value is measured after 48 hours, recovery at room temperature); 1000 hours at 125 C and 2 x UR applied 8 C/C: 15% after 48 hours recovery: C/C: 15% tan : 7% Rins: 500 M or RiCR 25 s, whichever is less after 48 hours recovery: C/C: 20% tan : 7% Rins: 1000 M or RiCR 50 s, whichever is less www.phycomp-components.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, X7R 10 V REVISION HISTORY Revision Date Change Notification Description Rev.5 2001 May 30 - - Converted to Phycomp brand 2001 May 30 Rev.5 9 www.phycomp-components.com