DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS Mid-voltage: NP0/X7R (Pb Free & RoHS compliant) 100 V TO 500 V Product specification - Sep 08, 2005 V. 0 10 pF to 470 nF Product specification Surface-Mount Ceramic Multilayer Capacitors SCOPE This specification describes Midvoltage NP0/X7R series chip capacitors with lead-free terminations. NP0/X7R 100 V to 500 V 2 16 ORDERING INFORMATION Part number is identified by the series, size, tolerance, packing style, TC material, rated voltage and capacitance value. YAGEO ORDERING CODE CC XXXX X X XXX X (1) APPLICATIONS PCs, hard disk, game PCs Power supplies LCD panel ADSL, modem Mid-voltage (2) (3) (4) B (5) X XXX (6) (7) (1) SIZE - INCH BASED (METRIC) 0603 (1608) 0805 (2012) 1206 (3216) 1210 (3225) FEATURES Supplied in tape on reel Nickel-barrier end termination 1808 (4520) 1812 (4532) (2) TOLERANCE J = 5% K = 10% (3) PACKING STYLE R = 7" paper tape K = 7" blister tape P = 13" paper tape F = 13" blister tape C = Bulk case (4) TC MATERIAL NP0 X7R (5) RATED VOLTAGE 0 = 100 V A = 200 V Y = 250 V B = 500 V (6) PROCESS B = BME N = NME (7) CAPACITANCE VALUE: First two for significant figures and 3rd for number of zero Letter "R" for decimal point www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 3 16 CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. terminations electrodes MLB457 ceramic material Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION Table 1 For dimension see Table 1 W T L2 L4 L1 L3 TYPE CC0603 CC0805 CC1206 CC1210 CC1808 CC1812 L1 (mm) 1.6 0.10 2.0 0.20 3.20.20 3.2 0.20 4.5 0.30 4.5 0.30 W (mm) 0.8 0.07 1.25 0.20 1.60.20 2.5 0.20 2.0 0.30 3.2 0.30 T (mm) MBB211 Fig. 2 Surface mounted multilayer ceramic capacitor dimension L2/L3 (mm) L4 (mm) Refer to table 2 to 7 min. 0.20 0.25 0.25 0.25 0.25 0.25 max. 0.50 0.75 0.75 0.75 0.75 0.75 min. 0.60 0.55 1.40 1.40 2.20 2.20 www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 4 16 CAPACITANCE RANGE & THICKNESS FOR NP0 100V Table 2 For NP0 100 V sizes from 0603 to 1812 CAPACITANCE (pF) 100 V 0603 0805 0.8 0.10 0.6 0.10 1206 1210 1808 1812 0.6 0.10 1.25 0.20 1.25 0.20 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 0.6 0.10 180 220 270 330 390 470 560 680 820 1,000 1,200 1,500 0.85 0.10 1,800 2,200 2,700 3,300 3,900 1.25 0.20 0.85 0.10 4,700 5,600 1.150.15 0.85 0.10 www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 5 16 Table 2 For NP0 100 V sizes from 0603 to 1812 (continued) CAPACITANCE (pF) 100 V 0603 0805 6,800 1206 1210 1808 1812 1.150.15 8,200 1.25 0.20 10,000 12,000 15,000 0.85 0.10 1.25 0.20 1.25 0.20 0.85 0.10 18,000 1.150.15 22,000 27,000 33,000 39,000 47,000 NOTE 1. Values in shaded cells indicate thickness class in mm. 2. Capacitance range < 10 pF is on request. CAPACITANCE RANGE & THICKNESS FOR NP0 200/250 V Table 3 For NP0 200/250 V sizes from 0603 to 1812 CAPACITANCE (pF) 200/250 V 0603 0805 1206 0.8 0.10 0.6 0.10 0.6 0.10 1210 1808 1812 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Table 3 Mid-voltage NP0/X7R 100 V to 500 V 6 16 For NP0 200/250 V sizes from 0603 to 1812 (continued) CAPACITANCE (pF) 200/250 V 0603 0805 0.8 0.10 0.85 0.10 1206 1210 1808 1812 220 270 330 390 0.6 0.10 470 560 1.25 0.20 680 820 0.8 0.10 1,000 0.85 0.10 1,200 1.25 0.20 1,500 1.25 0.20 1.150.15 1,800 0.8 0.10 2,200 1.25 0.20 0.85 0.10 1.25 0.20 2,700 1.25 0.20 3,300 1.150.15 3,900 0.85 0.10 4,700 1.25 0.20 1.150.15 5,600 6,800 8,200 10,000 NOTE 1. Values in shaded cells indicate thickness class in mm. 2. Capacitance range < 10 pF is on request. CAPACITANCE RANGE & THICKNESS FOR NP0 500 V Table 4 For NP0 500 V sizes from 0805 to 1812 CAPACITANCE (pF) 500 V 0805 1206 0.6 0.10 0.6 0.10 1210 1808 1812 10 12 15 18 22 27 www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 7 16 Table 4 For NP0 500 V sizes from 0805 to 1812 (continued) CAPACITANCE 500 V (pF) 0805 1206 0.6 0.10 0.6 0.10 1210 1808 1812 33 39 47 56 68 82 100 120 150 180 0.85 0.10 220 270 330 0.85 0.10 390 470 0.85 0.10 560 680 820 1.25 0.20 1.150.15 1,000 1,200 0.8 0.10 1,500 1,800 2,200 2,700 1.150.15 1.25 0.20 1.25 0.20 1.25 0.20 1.25 0.20 1.150.15 3,300 3,900 4,700 1.25 0.20 5,600 6,800 8,200 10,000 NOTE 1. Values in shaded cells indicate thickness class in mm. 2. Capacitance range < 10 pF is on request. www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 8 16 CAPACITANCE RANGE & THICKNESS FOR X7R 100V Table 5 For X7R 100 V sizes from 0805 to 1812 CAPACITANCE (pF) 100 V 0603 0805 1206 0.6 0.10 0.85 0.10 1210 1808 1812 100 150 220 330 470 680 1,000 0.8 0.10 1,500 2,200 3,300 4,700 6,800 10,000 15,000 22,000 33,000 47,000 0.85 0.10 1.25 0.20 68,000 100,000 0.85 0.10 1.150.15 0.85 0.10 150,000 1.150.15 220,000 1.6 0.20 1.25 0.20 1.150.15 330,000 470,000 1.6 0.20 680,000 1,000,000 NOTE 1. Values in shaded cells indicate thickness class in mm. www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 9 16 CAPACITANCE RANGE & THICKNESS FOR X7R 200/250 V Table 6 For X7R 200/250 V sizes from 0805 to 1812 CAPACITANCE (pF) 200/250 V 0805 1206 1210 1808 1812 100 150 220 330 470 680 1,000 0.85 0.10 1,500 2,200 3,300 0.85 0.10 4,700 6,800 10,000 1.25 0.20 15,000 0.8 0.10 22,000 1.25 0.20 33,000 47,000 68,000 100,000 0.85 0.10 1.150.15 1.150.15 1.25 0.20 1.25 0.20 1.25 0.20 1.150.15 150,000 220,000 1.6 0.20 330,000 2.0 0.20 470,000 680,000 1,000,000 NOTE 1. Values in shaded cells indicate thickness class in mm. www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 10 16 CAPACITANCE RANGE & THICKNESS FOR X7R 500 V Table 7 For X7R 500 V sizes from 0805 to 1812 CAPACITANCE (pF) 500 V 0805 1206 1210 1808 1812 100 150 220 330 470 680 1,000 0.8 0.10 1,500 1.150.15 2,200 3,300 4,700 1.150.15 0.85 0.10 6,800 10,000 1.25 0.20 1.25 0.20 15,000 1.25 0.20 22,000 33,000 47,000 1.150.15 1.25 0.20 1.6 0.20 1.25 0.20 68,000 100,000 1.6 0.20 150,000 220,000 330,000 470,000 680,000 1,000,000 NOTE 1. Values in shaded cells indicate thickness class in mm. www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors NP0/X7R Mid-voltage 100 V to 500 V 11 16 THICKNESS CLASSES AND PACKING QUANTITY Table 8 DESCRIPTION SIZE CODE THICKNESS CLASSIFICATION (mm) 8 mm TAPE WIDTH/AMOUNT PER REEL O180 mm, 7" O330 mm, 13" 12 mm TAPE WIDTH /AMOUNT PER REEL Paper Blister Paper Blister O180 mm, 7" Blister 0603 0.8 0.10 4,000 --- --- --- --- 0805 0.6 0.10 4,000 --- --- --- --- 0.8 0.10 4,000 --- --- --- --- 0.85 0.1 4,000 --- --- --- --- 1.25 0.20 --- 3,000 --- --- --- 0.6 0.10 4,000 --- 20,000 --- --- 0.8 0.10 4,000 --- --- --- --- 0.85 0.10 4,000 --- 15,000 --- --- 1.00 0.10 --- 3,000 --- 10,000 --- 1.15 0.15 --- 3,000 --- 10,000 --- 1.25 0.20 --- 3,000 --- --- --- 0.6 0.10 --- 4,000 --- 15,000 --- 0.85 0.10 --- 4,000 --- 10,000 --- 1.15 0.15 --- 3,000 --- 10,000 --- 1.25 0.20 --- 3,000 --- --- --- 1.6 0.20 --- 2,000 --- --- --- 1.15 0.15 --- --- --- --- 1,500 1.25 0.20 --- --- --- --- 3,000 1.35 0.15 --- --- --- --- 1,000 1.5 0.10 --- --- --- --- 1,000 1.6 0.20 --- --- --- --- 2,000 2.0 0.20 --- --- --- --- 2,000 0.85 0.10 --- --- --- --- 2,000 1.15 0.15 --- --- --- --- 1,500 1.25 0.20 --- --- --- --- 1,000 1.35 0.15 --- --- --- --- 1,000 1.5 0.1 --- --- --- --- 1,000 1.6 0.2 --- --- --- --- 1,000 2.0 0.20 --- --- --- --- 2,000 1206 1210 Mid / High voltage 1808 1812 www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 12 16 100 V to 500 V ELECTRICAL CHARACTERISTICS NP0/X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise stated all electrical values apply at an ambient temperature of 201 C, an atmospheric pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%. Table 9 VALUE DESCRIPTION Capacitance range (1) Capacitance tolerance (1) 10 pF to 470 nF : NP0 X7R Dissipation factor NP0 X7R 5% 10% (D.F.) (1): Insulation resistance after 1 minute at Ur (DC) 0.1% 2.5% Rins 10 G or Rins x C 500 seconds whichever is less Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): NP0 X7R Operating temperature range: NP0/X7R 30 ppm/C 15% -55 C to +125 C NOTE 1. NP0: frequency = 1 MHz for C 1 nF, measuring at voltage 1 Vrms; frequency = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms X7R: frequency = 1 KHz for C 10 F, measuring at voltage 1 Vrms. www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 13 16 TESTS AND REQUIREMENTS Table 10 Test condition, procedure and requirements TEST Mounting Visual inspection and dimension check Capacitance TEST METHOD PROCEDURE REQUIREMENTS IEC 6038421/22 4.3 The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage 4.4 Any applicable method using x 10 magnification In accordance with specification 4.5.1 NP0: f = 1 MHz for C 1 nF, measuring at voltage 1 Vrms at 20 C; f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 C Within specified tolerance X7R: f = 1 KHz for C 10 F, measuring at voltage 1 Vrms at 20 C Dissipation factor (D.F.) 4.5.2 NP0: f = 1 MHz for C 1 nF, measuring at voltage 1 Vrms at 20 C; f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 C In accordance with specification X7R: f = 1 KHz for C 10 F, measuring at voltage 1 Vrms at 20 C Insulation resistance Voltage proof 4.5.3 At Ur (DC) for 1 minute In accordance with specification 4.5.4.2 Test voltage (DC) applied for 1 minute No breakdown or flashover Ur 100 V: 2.5 x Ur applied to NP0/X7R series 100 V < Ur 200 V: 1.5 x Ur +100 V applied to NP0/X7R series 200 V < Ur 500 V: 1.3 x Ur +100 V applied to NP0/X7R series Ur > 500 V: 1.3 x Ur applied to NP0/X7R series I: 7.5 mA Temperature characteristic Adhesion 4.6 Between minimum and maximum temperature NP0: lC/Cl: 30 ppm/C X7R: lC/Cl: 15% 4.15 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate for size 0603: a force of 5 N applied for size 0402: a force of 2.5 N applied No visible damage www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 14 16 Table 10 Test condition, procedure and requirements (continued) TEST Bond strength of plating on end face TEST METHOD PROCEDURE REQUIREMENTS IEC 6038421/22 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm NP0: lC/Cl: 1% or 0.5 pF whichever is greater 4.8 X7R: lC/Cl: 10% Resistance to soldering heat 4.9 Precondition: 150 +0/-10 C for 1 hour, then keep for 24 1 hours at room temperature Preheating: for size 1206: 120 to 150 C for 1 minute Preheating: for size >1206: 100 to 120 C for 1 minute and 170 to 200 C for 1 minute Solder bath temperature: 260 5 C Dipping time: 10 0.5 seconds The termination shall be well tinned NP0: lC/Cl: 0.5% or 0.5 pF whichever is greater X7R: lC/Cl: 10% D.F.: within initial specified value Rins: within initial specified value Recovery time: 24 2 hours. Solderability 4.10 Unmounted chips completely immersed in a solder bath at 235 5 C The termination shall be well tinned. Dipping time: 2 0.5 seconds Depth of immersion: 10 mm Rapid change of temperature 4.11 Preconditioning; 150 +0/-10 C for 1 hour, then keep for 24 1 hours at room temperature No visual damage 5 cycles with following detail: 30 minutes at lower category temperature; 30 minutes at upper category temperature X7R: lC/Cl: 15% NP0: lC/Cl: 1% or 1 pF whichever is greater D.F.: within initial specified value Rins: within initial specified value Recovery time 24 2 hours. Damp heat, with Ur load 4.13 Initial measurements; after 150 +0/-10 C for 1 hour, then keep for 24 1 hours at room temperature NP0: lC/Cl: 2% or 1 pF whichever is greater Duration and conditions: 500 12 hours at 40 2 C; 90 to 95% RH; Ur applied X7R: lC/Cl: 15% Final measurement: perform a heat treatment at 150 +0/-10 C for 1 hour, final measurements shall be carried out 24 1 hours after recovery at room temperature without load. NP0: D.F.: 2 x initial value max. X7R 100 V: D.F. 5% NP0: Rins 2,500 M or Rins x Cr 25 seconds, whichever is less X7R: Rins 500 M or Rins x Cr 25 seconds, whichever is less www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 15 16 Table 10 Test condition, procedure and requirements (continued) TEST Endurance TEST METHOD PROCEDURE REQUIREMENTS IEC 6038421/22 Preconditioning; Initial measurements; after 150 +0/-10 C for 1 hour, then keep for 24 1 hours at room temperature NP0: lC/Cl: 2% or 1 pF whichever is greater 4.14 X7R: lC/Cl: 15% Duration and conditions: 1,000 12 hours at upper category temperature with 1.5 x Ur voltage applied NP0: D.F.: 2 x initial value max. Final measurement: perform a heat treatment at 150 +0/-10 C for 1 hour, final measurements shall be carried out 24 1 hours after recovery at room temperature without load. NP0: Rins 4,000 M or Rins x Cr 40 seconds, whichever is less X7R 100 V: D.F. 5% X7R: Rins 1,000 M or Rins x Cr 50 seconds, whichever is less www.yageo.com Sep 08, 2005 V.0 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 500 V 16 16 REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 0 - - New Sep 08, 2005 www.yageo.com Sep 08, 2005 V.0 Mouser Electronics Authorized Distributor Click to View Pricing, Inventory, Delivery & Lifecycle Information: Yageo: CC0805KRX7R9BB392 CC0805KRX7R9BB393 CC0805KRX7R9BB471 CC0805KRX7R9BB472 CC0805KRX7R9BB562 CC0805KRX7R9BB681 CC0805KRX7R9BB682 CC0805KRX7R9BB821 CC0805KRX7R9BB473 CC0805KRX7R9BB333 CC0805KRX7R9BB563 CC0805KRX7R8BB683 CC0805KRX7R0BB221 CC0805KRX7R0BB222 CC0805KRX7R0BB223 CC0805KRX7R0BB332 CC0805KRX7R7BB104 CC0805KRX7R7BB154 CC0805KRX7R7BB224 CC0805KRX7R7BB274 CC0805KRX7R8BB103 CC0805KRX7R9BB183 CC0805KRX7R9BB332 CC0805KRX7R9BB331 CC0805KRX7R9BB273 CC0805KRX7R9BB272 CC0805KRX7R9BB223 CC0805KRX7R8BB104 CC0805KRX7R9BB221 CC0805KRX7R9BB153 CC0805KRX7R9BB152 CC0805KRX7R9BB123 CC0805KRX7R9BB103 CC0805KRX7R9BB102 CC0805KRX7R9BB222 CC0805KRX7R0BB103 CC0805KRX7RABB222 CC0805KRX7R0BB102 CC0805KRX7RABB681 CC0805KRX7RABB471 CC0805KRX7RABB221 CC0805KRX7RABB102 CC0805KRX7R9BB104 CC0805KKX7R9BB224 CC0805KRX7R7BB474 CC0805KRX7R7BB184 CC0805KRX7R8BB154 CC0805KRX7R9BB124 CC0805KRX7R9BB823 CC0805KRX7R9BB391 CC0805KRX7R9BB271 CC0805KRX7R9BB561 CC0805KRX7R9BB683 CC0805KRX7R9BB182 CC0805KRX7RYBB102 CC0805KRX7R8BB224 CC0805KRX7R8BB473 CC0805KRX7R9BB122 CC0805KRX7R9BB822 CC0805KKX7R7BB684 CC0805KRX7R6BB224 CC0805KRX7R6BB474 CC0805KRX7R7BB124 CC0805KRX7R7BB223 CC0805KRX7R7BB332 CC0805KRX7R7BB472 CC0805KRX7R7BB473 CC0805KRX7R7BB683 CC0805KRX7R7BB823 CC0805KRX7R8BB102 CC0805KRX7R8BB152 CC0805KRX7R8BB183 CC0805KRX7R8BB184 CC0805KRX7R8BB223 CC0805KRX7R8BB332 CC0805KRX7R8BB333 CC0805KRX7R8BB393 CC0805KRX7R8BB471 CC0805KRX7R8BB823 CC0805KRX7R9BB101 CC0805KRX7R9BB151 CC0805KRX7R9BB154 CC0805KRX7R9BB181 CC0805KRX7R9BB201 CC0805KRX7R9BB202 CC0805KRX7R9BB224 CC0805KRX7R9BB301 CC0805KRX7RYBB221 CC0805KRX7RABB472 CC0805KRX7RYBB472 CC0805KRX7R0BB682 CC0805KRX7R0BB681 CC0805KRX7RYBB152 CC0805KRX7R0BB471 CC0805KRX7RYBB471 CC0805KRX7RYBB271 CC0805KRX7RABB331 CC0805KRX7R0BB271 CC0805KRX7RBBB102 CC0805KRX7RYBB222