SPECIFICATIO
N
(Reference sheet)
Supplier : Samsung electro-mechanics Samsung P/N : CL10A475KQ8NNNL
Product : Multi-layer Ceramic Capacitor Description : CAP, 4.7㎌, 6.3V, ±10%, X5R, 0603
CL 10 A 475 K Q 8 N N N L
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 0603 (inch code) L: 1.6 ± 0.1 mm W: ± 0.1 mm
③Dielectric X5R ⑧Inner electrode
④Capacitance 4.7 ㎌Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 6.3 V ⑩Special Reserved for future use
⑦Thickness 0.8 ± 0.1 mm ⑪Packaging Cardboard Type, 13" reel
B. Samsung Reliability Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2Vrms
Tan δ (DF) 0.1 max.
Insulation 10,000Mohm or 100Mohm㎌Rated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X5R
Characteristics (From -55℃ to 85℃, Capacitance change should be within ±15%)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Sn 100%
Cu
Ni
0.8
Performance Test condition
250%
A. Samsung Part Number
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0hrs
IR : 12.5㏁·㎌ or Over
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : 25㏁·㎌ or Over
1000+48/-0hrs
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
Product specifications included in the specifications are effective as of March 1, 2013.
Please be advised that they are standard product specifications for reference only.
We may change, modify or discontinue the product specifications without notice at any time.
So, you need to approve the product specifications before placing an order.
Should you have any question regarding the product specifications,
please contact our sales personnel or application engineers.
Performance Test condition
150%