NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR120AA Cylindrical 4/5AA size (HR 15/43) Dimensions (with Tube) (mm) 2.0 Charge: 600mA(1 It)1.2hrs. 1.9 1.8 Voltage (V) 1.7 +0 0.7 14.5 - 1.6 1.5 1.4 1.3 1.2 1.1 0C 20C 45C 1.0 (+) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 43.0 +- 01.0 Typical Discharge Characteristics 1.8 Charge: 1200mA(1 It)1.2hrs,20C DischargeTemperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 14.5+0/-0.7 0.57+0/-0.03 0.8 Height 43.0+0/-1.0 1.69+0/-0.04 Approximate Weight Grams Ounces 23 0.81 Nominal Voltage Average** Discharge Capacity* 1.2V 1.8 1220 mAh 1.7 240mA(0.2 It) 0 1 2 3 4 Discharge Time (hours) 5 6 Charge: 1200mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.6 Charge Charge 19m Standard 120mA (0.1It) x 16hrs. Rapid 1200mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1150 mAh Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.5 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 1200mA(1 It) 2400mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR150AA Cylindrical AA size (HR 15/51) Typical Charge Characteristics Dimensions (with Tube) (mm) 2.0 Charge: 1500mA(1 It)1.2hrs. 1.9 1.8 Voltage (V) 1.7 14.5 +- 00.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 50.5 +0 0 10 20 30 40 50 60 70 Charge Time (minutes) 80 90 100 Typical Discharge Characteristics 1.0 1.8 Charge: 1500mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 14.5+0/-0.7 0.57+0/-0.03 0.8 Height 50.0+0/-1.0 1.97+0/-0.06 Approximate Weight Grams Ounces 26 0.92 Nominal Voltage Average** Discharge Capacity* 1.8 1.7 1 2 3 4 Discharge Time (hours) 5 6 Charge: 1500mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.6 Charge Charge 20m Standard 150mA (0.1It) x 16hrs. Rapid 1500mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1500 mAh Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.2V 1580 mAh 300mA(0.2 It) 0 < 1 year < 3 months < 1 month C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C -20C to 55C F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F 1.5 1.4 1.3 1.2 1.1 1.0 1500mA(1 It) 3000mA(2 It) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR200A Cylindrical 4/5A size (HR 17/43) Dimensions (with Tube) (mm) 2.0 Charge: 1700mA(0.85 It)1.4hrs. 1.9 Voltage (V) 1.8 17.0 +- 00.7 1.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 0 10 20 30 40 50 60 70 80 Charge Time (minutes) 90 100 110 120 43.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 1700mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 17.0+0/-0.7 0.67+0/-0.03 0.8 0 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 32 1.13 Nominal Voltage Discharge Capacity* 1.2V 1.8 Average** 2040 mAh 1.7 Rated (Min.) 2000 mAh 2 3 4 Discharge Time (hours) 5 6 Charge: 1700mA(0.85 It)1.4hrs,20C Discharge Temperature: 20C Charge Charge 20m Standard 200mA (0.1It) x 16hrs. Rapid 2000mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1.6 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 400mA(0.2 It) 1 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 2000mA(1 It) 4000mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR200SCP Cylindrical 4/5SC size (HR 23/34) (mm) Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 23.0 +- 01.0 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 2000mA(1 It)1.2hrs. 0C 20C 40C 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 34.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.7 1.6 1.5 Voltage (V) ( ) Specifications 1.4 1.3 1.2 1.1 mm inch Diameter 23.0+0/-0.1 0.91+0/-0.04 Height 34.0+0/-1.5 1.34+0/-0.06 Approximate Weight Grams Ounces 42 1.48 1.0 0.9 Discharge Capacity* 1.2V Average** 2100 mAh Rated (Min.) 1900 mAh Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature Charge Charge Rapid 2000mA (1It) x 1.2 hrs. Rapid Discharge Storage < 2 years < 6 months 30 40 50 60 70 Discharge Time (minutes) 80 90 100 Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.3 200mA (0.1It) x 16hrs. 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 20 1.4 5m C 10 1.5 Standard Standard 2000mA(1 It) 1.6 F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F Voltage (V) Nominal Voltage 0.8 0 1.2 1.1 1.0 0.9 0.8 10A 20A 0.7 0.6 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR210A Cylindrical A size (HR 17/50) Dimensions (with Tube) (mm) 2.0 Charge: 2100mA(1 It)1.2hrs. 1.9 Voltage (V) 1.8 17.0 +- 00.7 1.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 0 50.0 +- 01.5 10 20 30 40 50 60 70 80 Charge Time (minutes) 90 100 110 120 Typical Discharge Characteristics 1.8 Charge: 2100mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.2 1.0 mm inch Diameter 17.0+0/-0.7 0.67+0/-0.03 Height 50.0+0/-1.5 1.97+0/-0.06 Approximate Weight Grams Ounces 38 1.34 Nominal Voltage 0.9 420mA(0.2 It) 0.8 0 1.2V 1.8 Average** 2200 mAh 1.7 Rated (Min.) 2100 mAh 1 2 3 4 Discharge Time (hours) 5 6 Charge: 2100mA(1 It)1.2hrs,20C Discharge Temperature: 20C Charge Charge 20m Standard 210mA (0.1It) x 16hrs. Rapid 2100mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1.6 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.3 1.1 Specifications Discharge Capacity* 1.4 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 2100mA(1 It) 4200mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR210AA/B Cylindrical AA size (HR 15/51) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 1100mA (0.55 It), -V=5mV Voltage (V) 1.8 14.5 +- 00.7 1.6 1.4 1.2 0C 20C 40C 1.0 (+) 0.8 0 20 40 60 80 100 120 140 160 Discharge Time (hrs.) Typical Discharge Characteristics 50.5 +- 01.0 1.8 1.7 Charge: 200mA(0.1 It) x 16 hrs., 20C Discharge Temperature: 20C Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 1.0 Specifications mm 14.5 +0/-0.7 0.57 +0/-0.3 Height 50.5 +0/-1.0 1.99 +0/-0.5 Approximate Weight Grams Ounces 29 1.02 2080mAh Rated (Min.) 2000mAh Ambient Temperature Charge Standard Rapid Discharge Storage 2 3 4 6 5 Charge: 1100mA (0.55It), -V, 20C Discharge Temperature: 20C 1.6 25m 200mA (0.1It) x 16 hrs. 1200mA (1It) x 2 hrs. 1.5 1.4 1.3 1.2 1.1 1.0 C F 0.9 0C to 45C 32F to 113F 0.8 0C to 40C 32F to 113F -10C to 65C 14F to 149F -20C to 35C -4F to 95F < 3 months -20C to 45C -4F to 113F < 1 month -20C to 55C -4F to 131F < 1 year 1 1.8 1.7 Voltage (V) Average** 0 Discharge Time (hours) 1.2V Nominal Voltage Approx. internal Impedance at 1000Hz at charged state. Standard Charge Rapid 0.8 inch Diameter Discharge Capacity* 400mA (0.2It) 0.9 4000mA 2000mA (1It) (2It) 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (min.) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR210AH Cylindrical A size (HR 17/50) Dimensions (with Tube) (mm) 2.0 1.9 Charge:210mA(0.1 It)16hrs. 1.8 Voltage (V) 1.7 1.6 1.5 1.4 1.3 1.2 1.1 +0 0.7 17.0 - -10C 25C 60C 1.0 (+) 0.9 0.8 0 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 50.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) Specifications 100 90 80 70 60 50 40 Diameter mm inch 17.0+0/-0.7 0.67+0/-0.03 Height 50.0+0/-1.5 1.97+0/-0.06 Approximate Weight Grams Ounces 38 1.34 2.0 1.9 1.8 Rated (Min.) 1900mAh 1.7 1.6 Ambient Temperature Charge Standard 210mA (0.1It) x 16 hrs. C F -10C to 60C 14F to 140F - - -10C to 60C 14F to 140F < 1 year -20C to 35C -4F to 95F < 3 months -20C to 45C -4F to 113F < 1 month -20C to 55C -4F to 131F < 1 week -20C to 60C -4F to 140F Rapid Discharge Storage 20m Voltage (V) 1.2V 2050mAh Approx. internal Impedance at 1000Hz at charged state. Standard Charge Rapid - 10 0 10 20 30 40 50 60 70 Temperature (C) Average2 Nominal Voltage Discharge Capacity1 30 - 20 Charge: 210mA(0.1 It)15hrs Disharge: 420mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 25C Charge: 210mA(0.1 It)16hrs,25C Disharge: 420mA(0.2 It) 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 0C 25C 60C 1 2 3 4 5 6 Charge Time (hours) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR250SCH Cylindrical SC size (HR 23/43) Dimensions (with Tube) (mm) 2.0 Charge: 0.1It x 15h at 25, 40, 60C Discharge: 0.1It to 1.0V at 25C Voltage (V) 1.8 23.0 +- 01.0 1.6 1.4 1.2 25C 40C 60C 1.0 (+) Rest: 3h 0.8 0 500 1000 1500 2000 2500 3000 3500 4000 4500 Capacity (mAh) 43.0 +- 01.5 Typical Discharge Characteristics 2.0 Charge: 0.5It x 2.4h at 25C Rest: 1h Discharge: 1, 2, 3It to 0.8V at 25C Voltage (V) 1.8 ( ) Specifications 1.4 1.2 mm inch Diameter 23.0+0/-1.0 0.91+0/-0.04 1.0 Height 43.0+0/-1.5 1.69+0/-0.06 0.8 Approximate Weight Grams Ounces Low Rate Charge Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week 55 1It 2It 3It 0 500 1000 1500 2000 2500 3000 3500 4000 4500 Capacity (mAh) 1.94 1.2V 2650 mAh 2500 mAh 5m 1.6 250mA x 16hrs. 1250mA x 2.4 hrs.4 125mA x 32 hrs. 83mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C Charge: 0.5It x 2.4h Rest: 1h Discharge: 10, 20, 30A to 0.8V at 20C 1.5 1.4 Voltage (V) Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Ambient Temperature 1.6 1.3 1.2 10A 1.1 20A 30A 1.0 0.9 0.8 0.7 0.6 0 500 1000 1500 2000 2500 3000 Capacity (mAh) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR260SCP Cylindrical SC size (HR 23/43) Dimensions (with Tube) (mm) 2.0 Charge: 2600mA x 1.2 hrs. Voltage (V) 1.8 23.0 +- 01.0 1.6 1.4 1.2 0C 20C 40C 1.0 (+) 0.8 0 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 0 43.0 +- 1.5 Typical Discharge Characteristics 1.8 Charge: 2600mA x 1.2 hrs., 20C Discharge: 2600mA, 0C, 20C, 40C Voltage (V) 1.6 ( ) Specifications mm inch Diameter 23.0+0/-1.0 0.91+0/-0.04 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 55 1.94 Charge Standard Rapid Discharge < 1 year Storage < 3 months < 1 month 1.2 1.0 0C 20C 40C 0.8 0 10 20 30 40 50 60 70 80 Discharge Time (minutes) 1.2V 2600 mAh 2450 mAh 5m 260mA x 16hrs. 2600mA x 1.2 hrs. F C 32F to 113F 0C to 45C 50F to 104F 10C to 40C -10C to 65C 14F to 149F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 1.8 Charge: 2600mA x 1.2 hrs., 20C Discharge: 10A, 20A, 20C 1.6 Voltage (V) Ambient Temperature Nominal Voltage Average2 Discharge 1 Rated (Min.) Capacity Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid 1.4 1.4 1.2 1.0 10A 20A 0.8 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR300CH Cylindrical C size (HR 26/50) for backup use Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 300mA(0.1 It) x 16hrs. Voltage (V) 1.8 1.6 1.4 1.2 25.8 +- 01.0 10C 25C 60C 1.0 (+) 0.8 0 2 4 6 8 10 20 30 40 50 60 60 70 Charge Time (hours) 50.0 +- 01.5 Typical Discharge Characteristics 120 Capacity Ratio (%) 110 ( ) Specifications mm inch 70 60 50 25.8+0/-1.0 1.02+0/-0.04 40 50.0+0/-1.5 1.97+0/-0.06 Grams Ounces 30 -20 Approximate Weight 80 2.82 3300 mAh Rated (Min.) 3100 mAh Charge 155mA x 32 hrs. 100mA x 48 hrs. Rapid Low Rate < 1 year < 3 months < 1 month 10 20 30 40 50 C F 0C to 45C 10C to 40C 32F to 113F 32F to 104F 14F to 149F 14F to 113F -10C to 45C -10C to 65C -20C to 35C -20C to 35C -20C to 55C Charge: 300mA(0.1It) x 16 hrs., 25C Discharge: 10A, 20A, 25C 1.6 Low Rate Discharge Storage 5m Rapid3 Standard 0 Temperature (C) Voltage (V) Charge -10 1.8 300mA (0.1It) x 16hrs. 1500mA (1It) x 2.4 hrs.4 Standard Charge: 300mA (0.1 It) x 16 hrs. Charge Temperature: -10 to 60C Discharge: 600mA (0.2 It) Cut-off Voltage: 1.0V Discharge Temperature: 25C 1.2V Average2 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 80 Height Nominal Voltage 2 90 Diameter Discharge Capacity1 1 100 1.4 1.2 1.0 10A 20A 0.8 0 5 10 15 20 25 30 Discharge Time (minutes) -4F to 95F -4F to 95F -4F to 131F After charging at 0.1It for 16 hours, discharging at 0.2It. For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR300SCP Cylindrical SC size (HR 23/43) (mm) Voltage (V) Dimensions (with Tube) 23.0 +- 01.0 ( +) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 3000mA(1 It)1.2hrs. 0C 20C 40C 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) Typical Discharge Characteristics +0 1.5 43.0 - 1.8 Charge: 3000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.4 1.3 1.2 1.1 1.0 Specifications 0.9 mm inch Diameter 23.0+0/-0.1 0.91+0/-0.04 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 57 2.01 3000mA(1 It) 0.8 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (minutes) 1.6 Discharge Capacity* 1.2V Average** 3050 mAh Rated (Min.) 2800 mAh Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature Charge Charge Standard 300mA (0.1It) x 16hrs. Rapid 3000mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage 4m < 2 years < 6 months C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.5 1.4 Voltage (V) Nominal Voltage 1.3 1.2 1.1 1.0 0.9 0.8 10A 20A 0.7 0.6 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR330APH Cylindrical L-Fat A size (HR 18/67) (mm) 2.0 1.9 Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 18.2 +- 00.7 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 (+) Charge: 330mA(0.1 It)16hrs. -10C 25C 60C 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 67.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) 80 70 60 40 Nominal Voltage Average2 Discharge 1 Rated (Min.) Capacity Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Low Rate Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week mm 18.2+0/-0.7 inch 0.72+0/-0.03 67.0+0/-1.5 Grams 2.64+0/-0.06 Ounces 60 2.12 30 - 20 Charge: 330mA(0.1 It)16hrs Disharge: 660mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 25C - 10 0 10 20 30 40 50 60 70 Temperature (C) 1.8 1.2V 3300 mAh 3200 mAh Charge: 330mA(0.1 It)16hrs, 20C Discharge Temperature: 20C 1.6 5.5m Voltage (V) Diameter Height Approximate Weight Ambient Temperature 90 50 Specifications Charge 100 330mA x 16hrs. 1650mA x 2.4 hrs.4 165mA x 32 hrs. 110mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1.4 10A 20A 1.2 1.0 0.8 0 5 10 15 20 25 30 Discharge Time (min.) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h Note: 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR370AH Cylindrical L-Fat A size (HR 18/67) (mm) 2.0 1.9 Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 18.2 +- 00.7 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 (+) Charge: 330mA(0.1 It)16hrs. -10C 25C 60C 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 67.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) 80 70 60 40 Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Low Rate Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week mm 18.2+0/-0.7 inch 0.72+0/-0.03 67.0+0/-1.5 Grams 2.64+0/-0.06 Ounces 60 2.12 30 - 20 Charge: 330mA(0.1 It)15hrs Disharge: 660mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 20C - 10 0 10 20 30 40 50 60 70 Temperature (C) 2.0 1.2V 3700 mAh 3500 mAh Charge: 330mA(0.1 It)16hrs,25C Disharge: 660mA(0.2 It) 1.9 1.8 20m Voltage (V) Diameter Height Approximate Weight Ambient Temperature 90 50 Specifications Charge 100 370mA x 16hrs. 1750mA x 2.4 hrs.4 185mA x 32 hrs. 123mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 0C 25C 60C 1 2 3 4 5 6 Charge Time (hours) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h Note: 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR380A Cylindrical L-A size (HR 17/67) Dimensions (with Tube) (mm) 2.0 1.9 Charge: 2000mA- V=10mV 1.8 Voltage (V) 1.7 17.0 +- 00.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 45C 1.0 0.9 0.8 0 20 40 60 80 100 120 140 160 Charge Time (minutes) 67.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch Diameter 17.0+0/-0.7 0.67+0/-0.03 Height 67.0+0/-1.5 2.64+0/-0.06 Approximate Weight Grams Ounces 53 1.87 Nominal Voltage Ambient Temperature Charge Standard Rapid Discharge Storage < 1 year < 3 months < 1 month 3 4 5 6 Charge: 2000mA,dT/dt=1.0C/min.20C Disharge Temperature: 20C 1.7 1.6 3700 mAh 25m 370mA (0.1It) x 16hrs. 2000mA dT/dt 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C -20C to 55C 2 1.8 3800 mAh C 1 Discharge Time (hours) Voltage (V) Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid*** 0.8 0 1.2V Average** Discharge Capacity* 760mA(0.2 It) 0.9 1.5 1.4 1.3 1.2 1.1 F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F 1.0 2000mA(0.53 It) 3800mA(1 It) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 110 120 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. *** For rapid charge: use dT/dt charge termination method. Refer to the Nickel Metal Hydride "Charge Methods" section for further details. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR450A Cylindrical L-fat A size (HR 18/67) (mm) Voltage (V) Dimensions (with Tube) 18.2+- 00.7 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 1500mA- V=10mV 0C 20C 45C 20 40 60 80 100 120 140 160 180 200 220 Charge Time (minutes) 67.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) Specifications inch Diameter 18.2+0/-0.7 0.72+0/-0.03 Height 67.0+0/-1.5 2.64+0/-0.06 Grams Ounces 60 2.12 Nominal Voltage Ambient Temperature Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid*** Standard Rapid Discharge < 1 year < 3 months < 1 month 0.9 900mA(0.2 It) 0.8 0 1 2 3 4 5 6 Discharge Time (hours) 1.2V 1.8 4500 mAh Average** Storage 1.2 1.0 1.6 25m 1.5 420mA (0.1It) x 16hrs. 2000mA dT/dt C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 4200 mAh F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F Voltage (V) Approximate Weight Charge 1.3 1.1 mm Discharge Capacity* 1.4 1.4 1.3 1.2 1.1 1.0 2000mA(0.44 It) 4500mA(1 It) 0.9 0.8 0 20 40 60 80 100 120 140 Discharge Time (minutes) -20C to 55C * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. *** For rapid charge: use dT/dt charge termination method. Refer to the Nickel Metal Hydride "Charge Methods" section for further details. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR60AAAH Cylindrical AAA size (HR 11/45) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 50mA x 16 hrs. 1.8 Voltage (V) 10.5 +- 00.7 (+) 1.6 1.4 1.2 10C 25C 60C 1.0 0.8 0 2 4 6 +0 1.0 44.5 - 8 10 12 14 16 18 20 60 70 Charge Time (hours) Typical Discharge Characteristics ( ) 120 Specifications mm inch Diameter 10.5 +0/-0.7 0.41 +0/-0.03 Height 44.5 +0/-1.0 1.75 +0/-0.04 Grams Ounces 13 0.46 Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Ambient Temperature Low Rate Charge Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week 100 90 80 70 60 50 40 30 -20 Charge: 50mA x 16 hrs. Charge Temperature: -10 to 60C Discharge: 100mA Cut off Voltage: 1.0V Discharge temperature: 25C -10 0 10 20 30 40 50 Temperature (C) 1.2V 550 mAh 500 mAh 35m 50mA x 16hrs. 250mA x 2.4 hrs.4 25mA x 32 hrs. 17mA x 48 hrs. C F 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 2.0 Charge: 500mA x 16 hrs. 25C Discharge: 100mA 1.8 Voltage (V) Approximate Weight Capacity Ratio (%) 110 10C 25C 60C 1.6 1.4 1.2 1.0 0.8 0 1 Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. 2 3 4 5 6 Discharge Time (hours) 3 Need specially designed control system Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR70AAAJ Cylindrical HR AAA size (HR 11/45) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 1.8 1.6 Voltage (V) 10.5 +- 00.7 Charge: 1It(650mA) x 1.2h at 0.20, 45C Rest: 1~3h Discharge: 1It(650mA) to 1.0V at 20C 1.4 1.2 (+) 1.0 0C 20C 45C 0.8 0 100 200 300 400 500 600 700 800 900 10001100 1200 Discharge Time (minutes) 44.5 +- 01.0 Typical Discharge Characteristics 2.0 Charge: 1It(650mA) x 1.2h at 20C Rest: 1h Discharge: 0.2It(130mA) to 1.0V at 20C Voltage (V) 1.8 ( ) Specifications inch Diameter 10.5+0/-0.7 0.41+0/-0.03 Height 44.5+0/-1.0 1.75+0/-0.04 Approximate Weight Grams Ounces 13 0.46 Ambient Temperature Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid Standard Rapid Discharge < 1 year < 3 months < 1 month 0.8 0 100 200 300 400 500 600 700 800 900 1000 1100 1200 Discharge Time (minutes) 2.0 720 mAh 1.8 Charge: 1It(650mA) x 1.2h at 20C Rest: 1 ~ 5h Discharge: 1It(650mA) to 1.0V at 20C 700 mAh 30m 70mA (0.1It) x 16hrs. 650mA (1It) x 1.2 hrs. F C 32F to 113F 0C to 45C 0C to 40C 32F to 104F 14F to 149F -10C to 65C -4F to 95F -20C to 35C -4F to 113F -20C to 45C -20C to 55C Voltage (V) Average** Storage 1.2 1.2V Nominal Voltage Charge 1.4 1.0 mm Discharge Capacity* 1.6 1.6 1.4 1.2 1.0 0.8 0 100 200 300 400 500 600 700 800 900 1000 11001200 Discharge Time (minutes) -4F to 131F * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR75AAA/B Cylindrical AAA size (HR 11/45) (mm) Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 10.5 +- 00.7 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 Charge: 450mA (0.64 It) x 1.7hrs 0 10 20 30 40 50 60 70 90 80 0C 20C 45C 100 110 120 Charge Time (minutes) 44.5 +- 01.0 Voltage (V) Typical Discharge Characteristics ( ) Specifications Diameter mm inch 10.5+0/-0.7 0.41+0/-0.03 Height 44.5+0/-1.0 1.75+0/-0.04 Approximate Weight Grams Ounces 12 0.42 Nominal Voltage Discharge Capacity* Charge: 450mA (0.64It) x 1.7 hrs, 20C. Discharge Temperature: 20C. 140mA (0.2It) 0 1 2 Average** 730 mAh Charge Rated (Min.) 700 mAh Voltage (V) Rapid 450mA x 1.7 hrs. Discharge Storage 35m 70mA x 16hrs. Rapid < 1 year < 3 months < 1 month 5 6 Charge: 450mA (0.64It) x 1.7hrs, 20C. Discharge Temperature: 20C. 1.6 Standard Standard 4 1.8 1.7 Charge 3 Discharge Time (hours) 1.2V Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 C F 0C to 45C 0C to 40C -10C to 65C -20C to 35C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -20C to 45C -20C to 55C -4F to 113F 1.5 1.4 1.3 1.2 1.1 1.0 700mA (1It) 1400mA (2It) 0.9 0.8 0 10 20 30 40 50 60 70 80 Discharge Time (hours) -4F to 131F * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR120AA Cylindrical 4/5AA size (HR 15/43) Dimensions (with Tube) (mm) 2.0 Charge: 600mA(1 It)1.2hrs. 1.9 1.8 Voltage (V) 1.7 +0 0.7 14.5 - 1.6 1.5 1.4 1.3 1.2 1.1 0C 20C 45C 1.0 (+) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 43.0 +- 01.0 Typical Discharge Characteristics 1.8 Charge: 1200mA(1 It)1.2hrs,20C DischargeTemperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 14.5+0/-0.7 0.57+0/-0.03 0.8 Height 43.0+0/-1.0 1.69+0/-0.04 Approximate Weight Grams Ounces 23 0.81 Nominal Voltage Average** Discharge Capacity* 1.2V 1.8 1220 mAh 1.7 240mA(0.2 It) 0 1 2 3 4 Discharge Time (hours) 5 6 Charge: 1200mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.6 Charge Charge 19m Standard 120mA (0.1It) x 16hrs. Rapid 1200mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1150 mAh Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.5 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 1200mA(1 It) 2400mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR150AA Cylindrical AA size (HR 15/51) Typical Charge Characteristics Dimensions (with Tube) (mm) 2.0 Charge: 1500mA(1 It)1.2hrs. 1.9 1.8 Voltage (V) 1.7 14.5 +- 00.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 50.5 +0 0 10 20 30 40 50 60 70 Charge Time (minutes) 80 90 100 Typical Discharge Characteristics 1.0 1.8 Charge: 1500mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 14.5+0/-0.7 0.57+0/-0.03 0.8 Height 50.0+0/-1.0 1.97+0/-0.06 Approximate Weight Grams Ounces 26 0.92 Nominal Voltage Average** Discharge Capacity* 1.8 1.7 1 2 3 4 Discharge Time (hours) 5 6 Charge: 1500mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.6 Charge Charge 20m Standard 150mA (0.1It) x 16hrs. Rapid 1500mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1500 mAh Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.2V 1580 mAh 300mA(0.2 It) 0 < 1 year < 3 months < 1 month C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C -20C to 55C F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F 1.5 1.4 1.3 1.2 1.1 1.0 1500mA(1 It) 3000mA(2 It) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR200A Cylindrical 4/5A size (HR 17/43) Dimensions (with Tube) (mm) 2.0 Charge: 1700mA(0.85 It)1.4hrs. 1.9 Voltage (V) 1.8 17.0 +- 00.7 1.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 0 10 20 30 40 50 60 70 80 Charge Time (minutes) 90 100 110 120 43.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 1700mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch 0.9 Diameter 17.0+0/-0.7 0.67+0/-0.03 0.8 0 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 32 1.13 Nominal Voltage Discharge Capacity* 1.2V 1.8 Average** 2040 mAh 1.7 Rated (Min.) 2000 mAh 2 3 4 Discharge Time (hours) 5 6 Charge: 1700mA(0.85 It)1.4hrs,20C Discharge Temperature: 20C Charge Charge 20m Standard 200mA (0.1It) x 16hrs. Rapid 2000mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1.6 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 400mA(0.2 It) 1 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 2000mA(1 It) 4000mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR200SCP Cylindrical 4/5SC size (HR 23/34) (mm) Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 23.0 +- 01.0 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 2000mA(1 It)1.2hrs. 0C 20C 40C 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 34.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.7 1.6 1.5 Voltage (V) ( ) Specifications 1.4 1.3 1.2 1.1 mm inch Diameter 23.0+0/-0.1 0.91+0/-0.04 Height 34.0+0/-1.5 1.34+0/-0.06 Approximate Weight Grams Ounces 42 1.48 1.0 0.9 Discharge Capacity* 1.2V Average** 2100 mAh Rated (Min.) 1900 mAh Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature Charge Charge Rapid 2000mA (1It) x 1.2 hrs. Rapid Discharge Storage < 2 years < 6 months 30 40 50 60 70 Discharge Time (minutes) 80 90 100 Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.3 200mA (0.1It) x 16hrs. 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 20 1.4 5m C 10 1.5 Standard Standard 2000mA(1 It) 1.6 F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F Voltage (V) Nominal Voltage 0.8 0 1.2 1.1 1.0 0.9 0.8 10A 20A 0.7 0.6 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR210A Cylindrical A size (HR 17/50) Dimensions (with Tube) (mm) 2.0 Charge: 2100mA(1 It)1.2hrs. 1.9 Voltage (V) 1.8 17.0 +- 00.7 1.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 40C 1.0 0.9 0.8 0 50.0 +- 01.5 10 20 30 40 50 60 70 80 Charge Time (minutes) 90 100 110 120 Typical Discharge Characteristics 1.8 Charge: 2100mA(1 It)1.2hrs,20C Discharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.2 1.0 mm inch Diameter 17.0+0/-0.7 0.67+0/-0.03 Height 50.0+0/-1.5 1.97+0/-0.06 Approximate Weight Grams Ounces 38 1.34 Nominal Voltage 0.9 420mA(0.2 It) 0.8 0 1.2V 1.8 Average** 2200 mAh 1.7 Rated (Min.) 2100 mAh 1 2 3 4 Discharge Time (hours) 5 6 Charge: 2100mA(1 It)1.2hrs,20C Discharge Temperature: 20C Charge Charge 20m Standard 210mA (0.1It) x 16hrs. Rapid 2100mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage Voltage (V) 1.6 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.3 1.1 Specifications Discharge Capacity* 1.4 < 1 year < 3 months < 1 month 1.5 1.4 1.3 1.2 1.1 1.0 F 0.9 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F 0.8 0 -20C to 55C -4F to 131F C 2100mA(1 It) 4200mA(2 It) 10 20 30 40 50 60 70 Discharge Time (minutes) 80 90 100 * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR210AA/B Cylindrical AA size (HR 15/51) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 1100mA (0.55 It), -V=5mV Voltage (V) 1.8 14.5 +- 00.7 1.6 1.4 1.2 0C 20C 40C 1.0 (+) 0.8 0 20 40 60 80 100 120 140 160 Discharge Time (hrs.) Typical Discharge Characteristics 50.5 +- 01.0 1.8 1.7 Charge: 200mA(0.1 It) x 16 hrs., 20C Discharge Temperature: 20C Voltage (V) 1.6 ( ) 1.5 1.4 1.3 1.2 1.1 1.0 Specifications mm 14.5 +0/-0.7 0.57 +0/-0.3 Height 50.5 +0/-1.0 1.99 +0/-0.5 Approximate Weight Grams Ounces 29 1.02 2080mAh Rated (Min.) 2000mAh Ambient Temperature Charge Standard Rapid Discharge Storage 2 3 4 6 5 Charge: 1100mA (0.55It), -V, 20C Discharge Temperature: 20C 1.6 25m 200mA (0.1It) x 16 hrs. 1200mA (1It) x 2 hrs. 1.5 1.4 1.3 1.2 1.1 1.0 C F 0.9 0C to 45C 32F to 113F 0.8 0C to 40C 32F to 113F -10C to 65C 14F to 149F -20C to 35C -4F to 95F < 3 months -20C to 45C -4F to 113F < 1 month -20C to 55C -4F to 131F < 1 year 1 1.8 1.7 Voltage (V) Average** 0 Discharge Time (hours) 1.2V Nominal Voltage Approx. internal Impedance at 1000Hz at charged state. Standard Charge Rapid 0.8 inch Diameter Discharge Capacity* 400mA (0.2It) 0.9 4000mA 2000mA (1It) (2It) 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (min.) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR210AH Cylindrical A size (HR 17/50) Dimensions (with Tube) (mm) 2.0 1.9 Charge:210mA(0.1 It)16hrs. 1.8 Voltage (V) 1.7 1.6 1.5 1.4 1.3 1.2 1.1 +0 0.7 17.0 - -10C 25C 60C 1.0 (+) 0.9 0.8 0 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 50.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) Specifications 100 90 80 70 60 50 40 Diameter mm inch 17.0+0/-0.7 0.67+0/-0.03 Height 50.0+0/-1.5 1.97+0/-0.06 Approximate Weight Grams Ounces 38 1.34 2.0 1.9 1.8 Rated (Min.) 1900mAh 1.7 1.6 Ambient Temperature Charge Standard 210mA (0.1It) x 16 hrs. C F -10C to 60C 14F to 140F - - -10C to 60C 14F to 140F < 1 year -20C to 35C -4F to 95F < 3 months -20C to 45C -4F to 113F < 1 month -20C to 55C -4F to 131F < 1 week -20C to 60C -4F to 140F Rapid Discharge Storage 20m Voltage (V) 1.2V 2050mAh Approx. internal Impedance at 1000Hz at charged state. Standard Charge Rapid - 10 0 10 20 30 40 50 60 70 Temperature (C) Average2 Nominal Voltage Discharge Capacity1 30 - 20 Charge: 210mA(0.1 It)15hrs Disharge: 420mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 25C Charge: 210mA(0.1 It)16hrs,25C Disharge: 420mA(0.2 It) 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 0C 25C 60C 1 2 3 4 5 6 Charge Time (hours) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR250SCH Cylindrical SC size (HR 23/43) Dimensions (with Tube) (mm) 2.0 Charge: 0.1It x 15h at 25, 40, 60C Discharge: 0.1It to 1.0V at 25C Voltage (V) 1.8 23.0 +- 01.0 1.6 1.4 1.2 25C 40C 60C 1.0 (+) Rest: 3h 0.8 0 500 1000 1500 2000 2500 3000 3500 4000 4500 Capacity (mAh) 43.0 +- 01.5 Typical Discharge Characteristics 2.0 Charge: 0.5It x 2.4h at 25C Rest: 1h Discharge: 1, 2, 3It to 0.8V at 25C Voltage (V) 1.8 ( ) Specifications 1.4 1.2 mm inch Diameter 23.0+0/-1.0 0.91+0/-0.04 1.0 Height 43.0+0/-1.5 1.69+0/-0.06 0.8 Approximate Weight Grams Ounces Low Rate Charge Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week 55 1It 2It 3It 0 500 1000 1500 2000 2500 3000 3500 4000 4500 Capacity (mAh) 1.94 1.2V 2650 mAh 2500 mAh 5m 1.6 250mA x 16hrs. 1250mA x 2.4 hrs.4 125mA x 32 hrs. 83mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C Charge: 0.5It x 2.4h Rest: 1h Discharge: 10, 20, 30A to 0.8V at 20C 1.5 1.4 Voltage (V) Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Ambient Temperature 1.6 1.3 1.2 10A 1.1 20A 30A 1.0 0.9 0.8 0.7 0.6 0 500 1000 1500 2000 2500 3000 Capacity (mAh) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR260SCP Cylindrical SC size (HR 23/43) Dimensions (with Tube) (mm) 2.0 Charge: 2600mA x 1.2 hrs. Voltage (V) 1.8 23.0 +- 01.0 1.6 1.4 1.2 0C 20C 40C 1.0 (+) 0.8 0 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) 0 43.0 +- 1.5 Typical Discharge Characteristics 1.8 Charge: 2600mA x 1.2 hrs., 20C Discharge: 2600mA, 0C, 20C, 40C Voltage (V) 1.6 ( ) Specifications mm inch Diameter 23.0+0/-1.0 0.91+0/-0.04 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 55 1.94 Charge Standard Rapid Discharge < 1 year Storage < 3 months < 1 month 1.2 1.0 0C 20C 40C 0.8 0 10 20 30 40 50 60 70 80 Discharge Time (minutes) 1.2V 2600 mAh 2450 mAh 5m 260mA x 16hrs. 2600mA x 1.2 hrs. F C 32F to 113F 0C to 45C 50F to 104F 10C to 40C -10C to 65C 14F to 149F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 1.8 Charge: 2600mA x 1.2 hrs., 20C Discharge: 10A, 20A, 20C 1.6 Voltage (V) Ambient Temperature Nominal Voltage Average2 Discharge 1 Rated (Min.) Capacity Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid 1.4 1.4 1.2 1.0 10A 20A 0.8 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR300CH Cylindrical C size (HR 26/50) for backup use Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 300mA(0.1 It) x 16hrs. Voltage (V) 1.8 1.6 1.4 1.2 25.8 +- 01.0 10C 25C 60C 1.0 (+) 0.8 0 2 4 6 8 10 20 30 40 50 60 60 70 Charge Time (hours) 50.0 +- 01.5 Typical Discharge Characteristics 120 Capacity Ratio (%) 110 ( ) Specifications mm inch 70 60 50 25.8+0/-1.0 1.02+0/-0.04 40 50.0+0/-1.5 1.97+0/-0.06 Grams Ounces 30 -20 Approximate Weight 80 2.82 3300 mAh Rated (Min.) 3100 mAh Charge 155mA x 32 hrs. 100mA x 48 hrs. Rapid Low Rate < 1 year < 3 months < 1 month 10 20 30 40 50 C F 0C to 45C 10C to 40C 32F to 113F 32F to 104F 14F to 149F 14F to 113F -10C to 45C -10C to 65C -20C to 35C -20C to 35C -20C to 55C Charge: 300mA(0.1It) x 16 hrs., 25C Discharge: 10A, 20A, 25C 1.6 Low Rate Discharge Storage 5m Rapid3 Standard 0 Temperature (C) Voltage (V) Charge -10 1.8 300mA (0.1It) x 16hrs. 1500mA (1It) x 2.4 hrs.4 Standard Charge: 300mA (0.1 It) x 16 hrs. Charge Temperature: -10 to 60C Discharge: 600mA (0.2 It) Cut-off Voltage: 1.0V Discharge Temperature: 25C 1.2V Average2 Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 80 Height Nominal Voltage 2 90 Diameter Discharge Capacity1 1 100 1.4 1.2 1.0 10A 20A 0.8 0 5 10 15 20 25 30 Discharge Time (minutes) -4F to 95F -4F to 95F -4F to 131F After charging at 0.1It for 16 hours, discharging at 0.2It. For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR300SCP Cylindrical SC size (HR 23/43) (mm) Voltage (V) Dimensions (with Tube) 23.0 +- 01.0 ( +) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 3000mA(1 It)1.2hrs. 0C 20C 40C 10 20 30 40 50 60 70 80 90 100 Charge Time (minutes) Typical Discharge Characteristics +0 1.5 43.0 - 1.8 Charge: 3000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.4 1.3 1.2 1.1 1.0 Specifications 0.9 mm inch Diameter 23.0+0/-0.1 0.91+0/-0.04 Height 43.0+0/-1.5 1.69+0/-0.06 Approximate Weight Grams Ounces 57 2.01 3000mA(1 It) 0.8 0 10 20 30 40 50 60 70 80 90 100 Discharge Time (minutes) 1.6 Discharge Capacity* 1.2V Average** 3050 mAh Rated (Min.) 2800 mAh Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature Charge Charge Standard 300mA (0.1It) x 16hrs. Rapid 3000mA (1It) x 1.2 hrs. Standard Rapid Discharge Storage 4m < 2 years < 6 months C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F Charge: 2000mA(1 It)1.2hrs,20C Disharge Temperature: 20C 1.5 1.4 Voltage (V) Nominal Voltage 1.3 1.2 1.1 1.0 0.9 0.8 10A 20A 0.7 0.6 0 2 4 6 8 10 12 14 16 18 20 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR330APH Cylindrical L-Fat A size (HR 18/67) (mm) 2.0 1.9 Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 18.2 +- 00.7 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 (+) Charge: 330mA(0.1 It)16hrs. -10C 25C 60C 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 67.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) 80 70 60 40 Nominal Voltage Average2 Discharge 1 Rated (Min.) Capacity Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Low Rate Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week mm 18.2+0/-0.7 inch 0.72+0/-0.03 67.0+0/-1.5 Grams 2.64+0/-0.06 Ounces 60 2.12 30 - 20 Charge: 330mA(0.1 It)16hrs Disharge: 660mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 25C - 10 0 10 20 30 40 50 60 70 Temperature (C) 1.8 1.2V 3300 mAh 3200 mAh Charge: 330mA(0.1 It)16hrs, 20C Discharge Temperature: 20C 1.6 5.5m Voltage (V) Diameter Height Approximate Weight Ambient Temperature 90 50 Specifications Charge 100 330mA x 16hrs. 1650mA x 2.4 hrs.4 165mA x 32 hrs. 110mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1.4 10A 20A 1.2 1.0 0.8 0 5 10 15 20 25 30 Discharge Time (min.) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h Note: 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR370AH Cylindrical L-Fat A size (HR 18/67) (mm) 2.0 1.9 Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 18.2 +- 00.7 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 (+) Charge: 330mA(0.1 It)16hrs. -10C 25C 60C 2 4 6 8 10 12 14 16 18 20 Charge Time (hours) Typical Discharge Characteristics 67.0 +- 01.5 120 Capacity Ratio (%) 110 ( ) 80 70 60 40 Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Low Rate Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week mm 18.2+0/-0.7 inch 0.72+0/-0.03 67.0+0/-1.5 Grams 2.64+0/-0.06 Ounces 60 2.12 30 - 20 Charge: 330mA(0.1 It)15hrs Disharge: 660mA(0.2 It),cut off voltage 1.0V Disharge Temperature: 20C - 10 0 10 20 30 40 50 60 70 Temperature (C) 2.0 1.2V 3700 mAh 3500 mAh Charge: 330mA(0.1 It)16hrs,25C Disharge: 660mA(0.2 It) 1.9 1.8 20m Voltage (V) Diameter Height Approximate Weight Ambient Temperature 90 50 Specifications Charge 100 370mA x 16hrs. 1750mA x 2.4 hrs.4 185mA x 32 hrs. 123mA x 48 hrs. F C 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 0C 25C 60C 1 2 3 4 5 6 Charge Time (hours) 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 3 Need specially designed control system Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h Note: 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR380A Cylindrical L-A size (HR 17/67) Dimensions (with Tube) (mm) 2.0 1.9 Charge: 2000mA- V=10mV 1.8 Voltage (V) 1.7 17.0 +- 00.7 1.6 1.5 1.4 1.3 1.2 1.1 (+) 0C 20C 45C 1.0 0.9 0.8 0 20 40 60 80 100 120 140 160 Charge Time (minutes) 67.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) 1.4 1.3 1.2 1.1 Specifications 1.0 mm inch Diameter 17.0+0/-0.7 0.67+0/-0.03 Height 67.0+0/-1.5 2.64+0/-0.06 Approximate Weight Grams Ounces 53 1.87 Nominal Voltage Ambient Temperature Charge Standard Rapid Discharge Storage < 1 year < 3 months < 1 month 3 4 5 6 Charge: 2000mA,dT/dt=1.0C/min.20C Disharge Temperature: 20C 1.7 1.6 3700 mAh 25m 370mA (0.1It) x 16hrs. 2000mA dT/dt 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C -20C to 55C 2 1.8 3800 mAh C 1 Discharge Time (hours) Voltage (V) Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid*** 0.8 0 1.2V Average** Discharge Capacity* 760mA(0.2 It) 0.9 1.5 1.4 1.3 1.2 1.1 F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F 1.0 2000mA(0.53 It) 3800mA(1 It) 0.9 0.8 0 10 20 30 40 50 60 70 80 90 100 110 120 Discharge Time (minutes) * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. *** For rapid charge: use dT/dt charge termination method. Refer to the Nickel Metal Hydride "Charge Methods" section for further details. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET Typical Charge Characteristics HHR450A Cylindrical L-fat A size (HR 18/67) (mm) Voltage (V) Dimensions (with Tube) 18.2+- 00.7 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 0 Charge: 1500mA- V=10mV 0C 20C 45C 20 40 60 80 100 120 140 160 180 200 220 Charge Time (minutes) 67.0 +- 01.5 Typical Discharge Characteristics 1.8 Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 1.6 Voltage (V) 1.5 ( ) Specifications inch Diameter 18.2+0/-0.7 0.72+0/-0.03 Height 67.0+0/-1.5 2.64+0/-0.06 Grams Ounces 60 2.12 Nominal Voltage Ambient Temperature Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid*** Standard Rapid Discharge < 1 year < 3 months < 1 month 0.9 900mA(0.2 It) 0.8 0 1 2 3 4 5 6 Discharge Time (hours) 1.2V 1.8 4500 mAh Average** Storage 1.2 1.0 1.6 25m 1.5 420mA (0.1It) x 16hrs. 2000mA dT/dt C 0C to 45C 0C to 40C -10C to 65C -20C to 35C -20C to 45C Charge: 2000mA dT/dt=1.0C/min,20C Disharge Temperature: 20C 1.7 4200 mAh F 32F to 113F 32F to 104F 14F to 149F -4F to 95F -4F to 113F -4F to 131F Voltage (V) Approximate Weight Charge 1.3 1.1 mm Discharge Capacity* 1.4 1.4 1.3 1.2 1.1 1.0 2000mA(0.44 It) 4500mA(1 It) 0.9 0.8 0 20 40 60 80 100 120 140 Discharge Time (minutes) -20C to 55C * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. *** For rapid charge: use dT/dt charge termination method. Refer to the Nickel Metal Hydride "Charge Methods" section for further details. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR60AAAH Cylindrical AAA size (HR 11/45) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 Charge: 50mA x 16 hrs. 1.8 Voltage (V) 10.5 +- 00.7 (+) 1.6 1.4 1.2 10C 25C 60C 1.0 0.8 0 2 4 6 +0 1.0 44.5 - 8 10 12 14 16 18 20 60 70 Charge Time (hours) Typical Discharge Characteristics ( ) 120 Specifications mm inch Diameter 10.5 +0/-0.7 0.41 +0/-0.03 Height 44.5 +0/-1.0 1.75 +0/-0.04 Grams Ounces 13 0.46 Nominal Voltage Average2 Discharge Rated (Min.) Capacity1 Approx. Internal impedance at 1000Hz at charged state. Standard Rapid3 Charge Ambient Temperature Low Rate Charge Standard Rapid Discharge < 1 year < 6 months Storage < 1 month < 1 week 100 90 80 70 60 50 40 30 -20 Charge: 50mA x 16 hrs. Charge Temperature: -10 to 60C Discharge: 100mA Cut off Voltage: 1.0V Discharge temperature: 25C -10 0 10 20 30 40 50 Temperature (C) 1.2V 550 mAh 500 mAh 35m 50mA x 16hrs. 250mA x 2.4 hrs.4 25mA x 32 hrs. 17mA x 48 hrs. C F 14F to 140F -10C to 60C 14F to 113F -10C to 45C -10C to 60C 14F to 140F -4F to 95F -20C to 35C -4F to 113F -20C to 45C -4F to 131F -20C to 55C -4F to 149F -20C to 65C 1 After charging at 0.1It for 16 hours, discharging at 0.2It. 2 For reference only. 2.0 Charge: 500mA x 16 hrs. 25C Discharge: 100mA 1.8 Voltage (V) Approximate Weight Capacity Ratio (%) 110 10C 25C 60C 1.6 1.4 1.2 1.0 0.8 0 1 Control System: dT/dt cut-off; 1 to 2C/min -UV cut-off; -UV per cell = 5 to 10 mV T-control; T=65C Rapid charger timer; 2.4h (at 1.25a) Trickle timer; within 2h 4 With control system Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. 2 3 4 5 6 Discharge Time (hours) 3 Need specially designed control system Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR70AAAJ Cylindrical HR AAA size (HR 11/45) Dimensions (with Tube) Typical Charge Characteristics (mm) 2.0 1.8 1.6 Voltage (V) 10.5 +- 00.7 Charge: 1It(650mA) x 1.2h at 0.20, 45C Rest: 1~3h Discharge: 1It(650mA) to 1.0V at 20C 1.4 1.2 (+) 1.0 0C 20C 45C 0.8 0 100 200 300 400 500 600 700 800 900 10001100 1200 Discharge Time (minutes) 44.5 +- 01.0 Typical Discharge Characteristics 2.0 Charge: 1It(650mA) x 1.2h at 20C Rest: 1h Discharge: 0.2It(130mA) to 1.0V at 20C Voltage (V) 1.8 ( ) Specifications inch Diameter 10.5+0/-0.7 0.41+0/-0.03 Height 44.5+0/-1.0 1.75+0/-0.04 Approximate Weight Grams Ounces 13 0.46 Ambient Temperature Rated (Min.) Approx. Internal impedance at 1000Hz at charged state. Standard Charge Rapid Standard Rapid Discharge < 1 year < 3 months < 1 month 0.8 0 100 200 300 400 500 600 700 800 900 1000 1100 1200 Discharge Time (minutes) 2.0 720 mAh 1.8 Charge: 1It(650mA) x 1.2h at 20C Rest: 1 ~ 5h Discharge: 1It(650mA) to 1.0V at 20C 700 mAh 30m 70mA (0.1It) x 16hrs. 650mA (1It) x 1.2 hrs. F C 32F to 113F 0C to 45C 0C to 40C 32F to 104F 14F to 149F -10C to 65C -4F to 95F -20C to 35C -4F to 113F -20C to 45C -20C to 55C Voltage (V) Average** Storage 1.2 1.2V Nominal Voltage Charge 1.4 1.0 mm Discharge Capacity* 1.6 1.6 1.4 1.2 1.0 0.8 0 100 200 300 400 500 600 700 800 900 1000 11001200 Discharge Time (minutes) -4F to 131F * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET HHR75AAA/B Cylindrical AAA size (HR 11/45) (mm) Voltage (V) Dimensions (with Tube) Typical Charge Characteristics 10.5 +- 00.7 (+) 2.0 1.9 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 Charge: 450mA (0.64 It) x 1.7hrs 0 10 20 30 40 50 60 70 90 80 0C 20C 45C 100 110 120 Charge Time (minutes) 44.5 +- 01.0 Voltage (V) Typical Discharge Characteristics ( ) Specifications Diameter mm inch 10.5+0/-0.7 0.41+0/-0.03 Height 44.5+0/-1.0 1.75+0/-0.04 Approximate Weight Grams Ounces 12 0.42 Nominal Voltage Discharge Capacity* Charge: 450mA (0.64It) x 1.7 hrs, 20C. Discharge Temperature: 20C. 140mA (0.2It) 0 1 2 Average** 730 mAh Charge Rated (Min.) 700 mAh Voltage (V) Rapid 450mA x 1.7 hrs. Discharge Storage 35m 70mA x 16hrs. Rapid < 1 year < 3 months < 1 month 5 6 Charge: 450mA (0.64It) x 1.7hrs, 20C. Discharge Temperature: 20C. 1.6 Standard Standard 4 1.8 1.7 Charge 3 Discharge Time (hours) 1.2V Approx. Internal impedance at 1000Hz at charged state. Ambient Temperature 1.8 1.7 1.6 1.5 1.4 1.3 1.2 1.1 1.0 0.9 0.8 C F 0C to 45C 0C to 40C -10C to 65C -20C to 35C 32F to 113F 32F to 104F 14F to 149F -4F to 95F -20C to 45C -20C to 55C -4F to 113F 1.5 1.4 1.3 1.2 1.1 1.0 700mA (1It) 1400mA (2It) 0.9 0.8 0 10 20 30 40 50 60 70 80 Discharge Time (hours) -4F to 131F * After charging at 0.1It for 16 hours, discharging at 0.2It. ** For reference only. Battery performance and cycle life are strongly affected by how they are used. In order to maximize battery safety, please consult Panasonic when determining charge / discharge specs, warning label contents and unit design. Note: [It] was previously expressed as [C]. [It] is an IEC standard expression for the amount of charge or discharge current and is expressed as: It(A) = Cn (Ah)/1h. * [It] is the reference test current in ampres * [Cn] is the rated capacity of the cell or battery in Ampere-hours. n = the time base [hours] for which the rated capacity is declared NICKEL METAL HYDRIDE HANDBOOK AUGUST 2005 This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to modification without notice. Contact Panasonic for the latest information. Mouser Electronics Authorized Distributor Click to View Pricing, Inventory, Delivery & Lifecycle Information: Panasonic: HHR-25SCHY03 HHR-300CHA03 HHR-75AAAB5B HHR-26SCPY01 HHR-330AHY01 HHR-370AHA05