• Supplier : Samsung electro-mechanics • Samsung P/N: CL05X105KQ5NNNC
• Product : Multi-layer Ceramic Capacitor •Description : CAP, 1㎌, 6.3V, ±10%, X6S, 0402
CL 05 X 105 K Q 5 N N N C
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 0402 (inch code) L: 1.0 ± 0.05 mm W: ± 0.05 mm
③Dielectric X6S ⑧Inner electrode
④Capacitance 1㎌Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 6.3 V ⑩Special Reserved for future use
⑦Thickness 0.5 ± 0.05 mm ⑪Packaging Cardboard Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2Vrms
Tan δ (DF) 0.1 max.
Insulation 10,000Mohm or 100Mohm⋅㎌Rated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (×10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X6S
Characterisitcs (From -55℃ to 105℃, Capacitance change shoud be within ±22%)
Adhesive Strength No peeling shall be occur on the 500g·F, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface 1) Sn63Pb37 solder
is to be soldered newly 235±5℃, 5±0.5sec.
2) SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±15% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Judgement Test condition
250%
SPECIFICATION
A. Samsung Part Number
0.5
Sn 100%
Cu
Ni
Vibration Test Capacitance change : within ±10% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours × 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0hrs
IR : 12.5㏁·㎌ or Over
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : 25㏁·㎌ or Over 1000+48/-0hrs
Temperature Capacitance change : within ±15% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperatur
e
→25℃
→Max. operating temperature →25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
Judgement Test condition
100%