SPECIFICATION (Reference sheet) Supplier : Samsung electro-mechanics Samsung P/N: CL05B105KQ5NQNC Product : Multi-layer Ceramic Capacitor Description : CAP, 1, 6.3V, 10%, X7R, 0402 A. Samsung Part Number Series Size CL 05 B 105 K Q 5 N Q N C Samsung Multi-layer Ceramic Capacitor 0402 (inch code) Dielectric X7R Capacitance 1 10 % Capacitance L: 1.0 0.1 tolerance Rated Voltage 6.3 V Thickness 0.5 0.1 mm mm 0.5 0.1 W: Inner electrode Ni Termination Cu Plating Sn 100% mm (Pb Free) Product Size Control Code Special Reserved for future use Packaging Cardboard Type, 7" reel B. Samsung Reliability Test and Judgement condition Judgement Test condition 110% Capacitance Tan (DF) Within specified tolerance 0.1 max. 1.00.2Vrms *A capacitor prior to measuring the capacitance is heat treated at 150+0/-10, and maintained in ambient air for 242 hours. 10,000Mohm or 100Mohm Whichever is Smaller Rated Voltage Resistance Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Visual inspection 250% of the rated voltage Voltage mechanical breakdown Temperature X7R Characteristics Adhesive Strength (From -55 to 125, Capacitance change should be within 15%) No peeling shall be occur on the 500g*F, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Insulation within 12.5% 60~120 sec. Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Judgement Vibration Test Capacitance change : within 5% Tan , IR : initial spec. Moisture Capacitance change : Resistance Tan : 0.125 max IR Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours x 3 direction (x, y, z) within 12.5% With rated voltage 402, 90~95%RH, 500+12/-0hrs : 500Mohm or 12.5 Mohm Whichever is Smaller High Temperature Capacitance change : Resistance Tan : 0.125 max IR Test condition within 12.5% Capacitance change : Cycling Tan , IR : initial spec. of the rated voltage Max. operating temperature : 1,000Mohm or 25Mohm Whichever is Smaller Temperature With 150% within 7.5% 1000+48/-0hrs 1 cycle condition Min. operating temperature 25 25 Max. operating temperature 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.