MULTILAYER CERAMIC CAPACITORS
Middle and High Voltage Series (200V to 3kV)
Revision O
Mar. 09 2010 2/10
WALSIN TECHNOLOGY CORPORATION
566-1,Kao-Shi Road, 5 Lin, Yang-Mei, Tao-Yuan, Taiwan
5. EXTERNAL DIMENSIONS
6. GENERAL ELECTRICAL DATA
Dielectric NP0 X7R Y5V
Size 0603, 0805, 1206, 1210, 1808, 1812 0805, 1206, 1210, 1812
Capacitance* 0.5pF to 6800pF 100pF to 0.47µF 0.01µnF to 0.68µF
Capacitance tolerance***
Cap≤5pF: C (±0.25pF)
5pF<Cap<10pF: D (±0.5pF)
Cap≥10pF: J (±5%), K (±10%)
K (±10%), M (±20%) Z (-20/+80%)
Rated voltage (WVDC) 200V to 3kV 200V, 250V
Q* Cap<30pF: Q≥400+20C
Cap≥30pF: Q≥1000 ≤2.5% ≤5%
Insulation resistance at Ur** Ur=200~630V: ≥10GΩ or RxC≥100Ω-F whichever is smaller
Ur=1000~3000V: ≥10GΩ
Dielectric strength
200~300V: ≥2 x WVDC
500~999V: ≥1.5 x WVDC
1000~3000V: ≥1.2 x WVDC
Operating temperature -55 to +125°C -25 to +85°C
Capacitance characteristic ±30ppm ±15% +30/-80%
Termination Ni/Sn (lead-free termination)
* Measured at the condition of 30~70% related humidity.
NP0: Apply 1.0±0.2Vrms, 1.0MHz±10% for Cap≤1000pF and 1.0±0.2Vrms, 1.0kHz±10% for Cap>1000pF, 25°C at ambient temperature
X7R, Y5V: Apply 1.0±0.2Vrms, 1.0kHz±10%, at 20°C ambient temperature.
** Measured at 500VDC for 60 sec. for Ur>500VDC.
*** Preconditioning for Class II MLCC: Perform a heat treatment at 150±10°C for 1 hour, then leave in ambient condition for 24±2 hours
before measurement.
T
W
M
M
Fig. 1 The outline of MLCC
Size
Inch (mm) L (mm) W (mm) T (mm)/Symbol Remark
M
B
(mm)
0603(1608)
1.60±0.10 0.80±0.10 0.80±0.07
S 0.40±0.15
0.60±0.10
A
0.80±0.10
B
0805 (2012)
2.00±0.15 1.25±0.10
1.25±0.10
D #
0.50±0.20
0.80±0.10
B
0.95±0.10
C
3.20±0.15 1.60±0.15
1.25±0.10
D #
1206 (3216)
3.20±0.20 1.60±0.20 1.60±0.20
G #
0.60±0.20
0.95±0.10
C #
3.20±0.30 2.50±0.20 1.25±0.10
D #
1.60±0.20
G #
1210 (3225)
3.20±0.40 2.50±0.30 2.50±0.30
M #
0.75±0.25
1.25±0.10
D #
1808 (4520)
4.50+0.5/-0.3
2.03±0.25 2.00±0.20
K # 0.50±0.25
1.25±0.10
D #
1.60±0.20
G #
1812 (4532)
4.50+0.5/-0.3
3.20±0.30
2.00±0.20
K #
0.50±0.25
# Reflow soldering only is recommended.