DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS Class 2, Z5U Product Specification - Jul 08, 2003 V.6 25/50 V Phycomp Product specification Surface-mount ceramic multilayer capacitors FEATURES * Four standard sizes Class 2, Z5U 25/50 V QUICK REFERENCE DATA DESCRIPTION VALUE * For high frequency applications Rated voltage UR (DC) 25 V, 50 V * Supplied in tape on reel Capacitance range (E3 series): 10 nF to 470 nF * Nickel-barrier end terminations. Tolerance on capacitance after 1000 hours 20% (M); -20% to +80% (Z) APPLICATIONS Test voltage (DC) for 1 minute 2.5 x UR * Tuners Sectional specifications IEC 60 384-10, second edition 1989-04; also based on CECC 32 100 * Video recorders Detailed specification based on CECC 32 101-801 * All types of cameras Climatic category (IEC 60068) 10/85/21 * Television receivers * Telecommunications * Automotive * Data processing. terminations DESCRIPTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. electrodes The inner electrodes are connected to the two terminations and finally covered with a layer of plated tin (NiSn). A cross section of the structure is shown in Fig.1. MLB457 ceramic material Fig.1 2003 Jul 08 Rev.6 Construction of a ceramic multilayer capacitor. 2 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V MECHANICAL DATA W T L2 L4 L3 MBB211 L1 For dimensions see Table 1. Fig.2. Component outline. Physical dimensions Table 1 Capacitor dimensions L1 CASE SIZE L2 and L3 T MIN. MAX. MIN. MAX. L4 MIN. 0.73 0.87 0.25 0.65 0.40 W Dimensions in millimetres 1.6 0.10 0.8 0.07 0805 2.0 0.1 1.25 0.1 0.50 1.35 0.25 0.75 0.55 1206 3.2 0.15 1.6 0.15 0.50 1.25 0.25 0.75 1.40 1210 3.2 0.20 2.5 0.20 0.50 1.30 0.25 0.75 1.40 0603 Dimensions in inches 0603 0.063 0.004 0.032 0.003 0.029 0.035 0.010 0.026 0.016 0805 0.079 0.004 0.049 0.004 0.020 0.053 0.010 0.030 0.022 1206 0.126 0.006 0.063 0.006 0.020 0.049 0.010 0.030 0.056 1210 0.126 0.008 0.098 0.008 0.020 0.051 0.010 0.030 0.056 2003 Jul 08 Rev.6 3 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V SELECTION CHART C (nF) LAST TWO DIGITS OF 12NC 10 36 22 41 47 45 100 49 220 54 470 58 25 V 50 V 0603 0805 1206 0.80 0.07 0.60 0.10 1210 0.60 0.10 0.50 to 1.0 Note 1. Values in shaded cells indicate thickness class. Thickness classification and packing quantities THICKNESS CLASSIFICATION (mm) 8 mm TAPE WIDTH QUANTITY PER REEL 180 mm; 7" 330 mm; 13" QUANTITY PER BULK CASE PAPER BLISTER PAPER BLISTER 0603 0805 0.60 0.10 4 000 - 20 000 - - 10 000 0.80 0.07 4 000 - 15 000 - 15 000 - 0.50 to 1.0 - 4 000 - 10 000 - - 2003 Jul 08 Rev.6 4 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V ORDERING INFORMATION Components may be ordered by using either Phycomp's unique 12NC or a simple 15-digit clear text code. Ordering code 12NC (preferred) 2 2 X X 6 2 X X 8 X X X Carrier type 22 blister 38 paper 54 bulk Capacitance value(1) Size 5 0603 (25 V) 0 0805 (50 V) 1 1206 (50 V) 2 1210 (50 V) Packaging(2) 1 reel: 180 mm; 7" 5 reel: 330 mm; 13" 4 bulk case Tolerance 7 20% 8 -20% to +80% scm003 (1) Refer to chapter "Selection chart". (2) Quantity on reel depends on thickness classification, see section "Thickness classification and packing quantities". Clear text code EXAMPLE: 12062E104M9B20D Size Code 0603 0805 1206 1210 Temp. Char. Capacitance Tol. Vol. Termination 2E = Z5U 104=1000000 M = 20% 8 = 25V B = NiSn pF; the third Z = -20%/+80% 9 = 50V digit signifies the number of zeros Packing 2 = 180 mm; 7" paper Marking Series 0 = no marking D = BME 3 = 330 mm; 13" paper B = 180 mm; 7" blister F = 330 mm; 13" blister P = bulk case 2003 Jul 08 Rev.6 5 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V ELECTRICAL CHARACTERISTICS Class 2 capacitors; Z5U dielectric; NiSn terminations Unless otherwise stated all electrical values apply at an ambient temperature of 25 1 C, an atmospheric pressure of 86 to 105 kPa, and a relative humidity of 63 to 67%. DESCRIPTION VALUE Capacitance range (E3 series); note 1 25 V 50 V case size 0603 10 nF to 100 nF - case size 0805 - 10 nF to 100 nF case size 1206 - 10 nF to 220 nF case size 1210 - 100 nF 470 nF Tolerance on capacitance after 1000 hours 20% (M); -20% / +80% (Z) Tan ; note 1 4% Insulation resistance after 1 minute at UR (DC) Rins > 10 G or Rins x C > 1000 seconds, whichever is smaller Maximum capacitance change with respect to capacitance at 25 C (for typical values see Fig.5) +22% to -56% Ageing per time decade 4% Resistance to soldering heat 260 C; 10 seconds 3% Note 1. Measured at 25 C, 0.5 Vrms and 1 kHz, using a four-gauge method. 2003 Jul 08 Rev.6 6 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V CCA709 0 C C (%) -10 CCA710 600 tan (x 10-4) 500 -20 400 -30 300 -40 200 -50 100 -60 -70 0 10 0 20 30 0 VDC (V) Fig.3 C C (%) Typical capacitance change with respect to the capacitance at 1 V as a function of DC voltage at 25 C. Fig.4 20 40 60 80 100 T (C) Typical tan as a function of temperature. CCA711 10 0 -10 -20 -30 -40 -50 -60 20 0 Fig.5 40 60 80 100 T (C) Typical capacitance change as a function of temperature. 2003 Jul 08 Rev.6 7 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V TESTS AND REQUIREMENTS Table 2 Test procedures and requirements IEC 60384-10/ CECC 32 100 CLAUSE IEC 60068-2 TEST METHOD TEST PROCEDURE REQUIREMENTS 4.4 mounting the capacitors may be mounted on printed-circuit boards or ceramic substrates by applying wave soldering, reflow soldering (including vapour phase soldering) or conductive adhesive no visible damage 4.5 visual inspection and dimension check any applicable method using x10 magnification in accordance with specification 4.6.1 capacitance f = 1 kHz; measuring voltage 0.5 Vrms at 25 C within specified tolerance measured 1000 hours after date of manufacture 4.6.2 tan f = 1 kHz; measuring voltage 0.5 Vrms at 25 C in accordance with specification 4.6.3 insulation resistance at UR (DC) for 1 minute in accordance with specification 4.6.4 voltage proof 2.5 x UR for one minutes max. no breakdown or flashover 4.7.1 temperature characteristic 10 to 85 C C/C: +22% to -56% at 25 C 4.8 adhesion a force of 5 N applied for 10 s to the line joining the terminations and in a plane parallel to the substrate no visible damage 4.9 bond strength of plating on end face mounted in accordance with CECC 32 100, paragraph 4.4 no visible damage conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm C/C: 30% 2003 Jul 08 Rev.6 8 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors IEC 60384-10/ CECC 32 100 CLAUSE IEC 60068-2 TEST METHOD 4.10 Tb Class 2, Z5U 25/50 V TEST resistance to soldering heat PROCEDURE 260 5 C for 10 0.5 s in a static solder bath REQUIREMENTS the terminations shall be well tinned after recovery C/C: 20% tan : original specification Rins: original specification resistance to leaching 260 5 C for 30 1 s in a static solder bath using visual enlargement of x10, dissolution of the terminations shall not exceed 10% 4.11 Ta solderability zero hour test, and test after storage (20 to 24 months) in original packing in normal atmosphere; unmounted chips completely immersed for 2 0.5 s in a solder bath at 235 5 C the terminations shall be well tinned 4.14 Ca damp heat initialization: 150 C for 1 hour, recovery 48 4 hours at 40 C; 90 to 95% RH; UR applied for 500 hours C/C: 30% 4.15 2003 Jul 08 Rev.6 endurance initialization: 2 x UR at 85 x C for 1 hour (initial value) is measured after 48 4 hours; 2 x UR at 85 C for 42 days, recovery 48 4 hours at room temperature 9 tan : 6% max. Rins: 1000 M or RiCR 100 s, whichever is less after 48 hours recovery: C/C: 30% tan :6% max. Rins: 1000 M or RiCR 100 s, whichever is less www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Z5U 25/50 V REVISION HISTORY Revision Date Change Notification Description Rev.4 2001 Mar 30 - - Converted to Phycomp brand - Capacitance range changed from E12 to E3 series. Rev.5 2003 Jan 07 22/02/2001 - 470 nF 1206 no longer supported. - - Combined 25V and 50V data sheets - Updated company logo Rev.6 2003 Jul 08 - - 1206 size 25V phase out - 0805 220nF 50V phase out - 1210 1uF 50V phase out 2003 Jul 08 Rev.6 10 www.yageo.com