No
TCN-340S006E
TA-I
Thick Film Chip Resistor Arrays
Thick Film Chip Resistor Networks
(Lead-Free for CN34 Series) page
5/10
TA-I TECHNOLOGY CO., LTD
Note* : RCWV : Rated continuous working voltage
.
6.Marking
6.1 ±
±±
±5%(E24)
Resistance value is expressed by 3 digits, the first two digits represent the
significant figures of nominal resistance value in
Ω
, and the third digit
represents exponent for base of 10.
E.G. 472 = 47×10
2
= 4700Ω = 4.7KΩ
6.2 ±
±±
±1% (E96 )
Resistance value is expressed by 3 digits, the first three digits represent the
significant figures of nominal resistance value in
Ω
, and the fourth digit
represents exponent for base of 10.
E.G. 4701 = 470×10
1
= 4700Ω = 4.7kΩ
Whisker
SONY
SS-00254-8
Component , Lead-
Solder Heat Resistance Test for SMD. Lead-
Free Soldering “
Temp. Cycles :
-55
℃
(30 min.) / +155
℃
(30 min. )
Testing duration : 500
±
4 hours
Temp. Humidity Chambers:
Temperature : 85
℃
Humidity : 85% RH
Testing duration : 500
±
4 hours
.
Whisker formation :
50 um or less .
Resistance to Solder Heat
SONY
SS-00254-5
Component , Lead-Free Soldering part 5
Solder Heat Resistance Test for SMD. Lead-
Free Soldering “
Flow Solder :
Pre – heat : 100 to 105
℃
30
±
5 sec
Temperature : 260
±
3
℃
10 +1/ -0 sec
The entire sample shall be dipped in solder.
The specimen shall be stored at standard
atmospheric conditions for 1 hour .
Iron Solder :
Bit temperature : 350
±
10
℃
Application time of soldering iron : 3 +1/- 0sec
Apply the soldering iron to the electrode .
The specimen shall be stored at standard
atmospheric conditions for 1 hour , after
which the measurements shall be made
Electrical characteristics shall be
Satisfied .
Without distinct deformation in
appearance